SABIC Innovative Plastics LNP LUBRILOY RA2 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY RA2 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRILOY* RA2 is a compound based on Nylon 66 resin containing Aramid Fiber. Added feature of this material is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 6.89 GPa | 999 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 87.0 MPa | 12600 psi | ASTM D790 |
| Flexural Modulus | 2.62 GPa | 380 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Compressive Strength | 68.0 MPa | 9860 psi | SABIC Method |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.87 J/cm | 11.0 ft-lb/in | ASTM D4812 |
| Coefficient of Friction, Dynamic | 0.66 | 0.66 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.41 | 0.41 | ASTM D3702 Modified |
| K (wear) Factor | 10.1 x 10-8 mm³/N-M | 5.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 4.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
2.22 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 6.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
3.33 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C @Thickness 3.20 mm |
219 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Prodways PLASTCure Cast 100 3D Printing Polymer
- SABIC Innovative Plastics EXTEM UH1026 TPI Blend
- PolyOne Synprene® RT-5180 Styrene Butadiene Block Copolymer (SBC) (discontinued **)
- ELASTO UK Dryflex® 502550S SEBS Based Material, Unfilled Qualities, 55A Hardness, Black
- 3M FV038 Indoor UL Recognized White Vinyl Label Products
- Huntsman PE 1253 EVA Film Extrusion (discontinued **)
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 1.0 PHR Thanecure ZM
Copyright © lookpolymers.com All Rights Reserved