SABIC Innovative Plastics LNP LUBRICOMP ZX89743 PPE+PS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP ZX89743 PPE+PS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* ZX89743 is a compound based on PPE+PS Blend resin containing Glass Fiber, Glass Beads and a Proprietary Lubricant. Added features include : Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0036 cm/cm | 0.0036 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 74.0 MPa | 10700 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 5.30 GPa | 769 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 108 MPa | 15700 psi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-1 @Thickness 1.60 mm |
V-1 @Thickness 0.0630 in |
UL 94 |
Users viewing this material also viewed the following:
- Mallard Creek Polymers ROVENE® 5044 SBR Latex
- SABIC Innovative Plastics LNP LUBRICOMP EFL24P PEI
- Schwartz Technical Plastics LAMINEX® 2101 Cotton Fabric, Phenolic Resin Impregnated
- SGL Carbon Group Ridurid® EK 60 High Performance Graphite Filled Plastic
- Stir SpA Z 2000 DR AT MOD (PVC)
- A. Schulman POLYTROPE™ TPP 1010HF-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer
- DuPont Performance Polymers Delrin® 100STE NC010 Acetal (POM) (Unverified Data**)
- Eurotec® Tecomid® NB40 GR50 NL IL PA6, 50% glass fiber reinforced, impact modified, natural
Copyright © lookpolymers.com All Rights Reserved