Fainplast Compounds RE 520/1 Rigid PVC, Extrusion
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Extruded |
| Manufacturer | Fainplast Compounds |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fainplast Compounds RE 520/1 Rigid PVC, Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Electric pipes
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 - 1.55 g/cc | 0.0546 - 0.0560 lb/in³ | ISO R 1184 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | ISO R 527 |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | ISO R527 |
| Elongation at Break | 120 % | 120 % | ISO R 527 |
| Izod Impact, Unnotched | 0.500 - 0.900 J/cm @Temperature 23.0 °C |
0.937 - 1.69 ft-lb/in @Temperature 73.4 °F |
ISO R180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 83.0 - 85.0 °C @Load 5.00 kg |
181 - 185 °F @Load 11.0 lb |
ISO R306 |
Users viewing this material also viewed the following:
- Phillips 66 COPYLENE® CH085S Polypropylene, Homopolymer, Cast Film, Slip
- Kazanorgsintez 102-17 Composition of Low Density Polyethylene, Crack-Proof
- Kazanorgsintez E-14 Petroleum Resin
- A. Schulman POLYFORT™ FPP 809 Talc Filled Homopolymer Polypropylene
- Wellman Wellamid® GSF1849-N1 Nylon 66, 40% Glass Sphere/Fiber Reinforced
- Westlake EC474AA Low Density Polyethylene
- Cyclics CBT® 200 Thermoplastic Resin
- Ensinger Tecapeek® MT CF 30 Polyetheretherketone (PEEK)
- Fainplast Compounds Hax™ HFC 0108/4 Flame Retardant Polyolefin Cable Compound
Copyright © lookpolymers.com All Rights Reserved