SABIC Innovative Plastics LNP LUBRICOMP RX05487 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RX05487 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RX05487 is a compound based on Nylon 66 containing 10% Aramid Fiber, 10% Lubricant. Added features of this material are: Low Warpage, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| 1.21 g/cc | 0.0437 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.730 % | 0.730 % | 50% RH, 24 hrs; ASTM D570 |
| 1.10 % | 1.10 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 79.0 MPa | 11500 psi | 5 mm/min; ISO 527 |
| 81.0 MPa | 11700 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | 5 mm/min; ISO 527 |
| 81.0 MPa | 11700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 8.3 % | 8.3 % | Type I, 5 mm/min; ASTM D638 |
| 8.9 % | 8.9 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 8.2 % | 8.2 % | Type I, 5 mm/min; ASTM D638 |
| 8.9 % | 8.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.62 GPa | 525 ksi | 1 mm/min; ISO 527 |
| 3.71 GPa | 538 ksi | 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 102 MPa | 14800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.27 GPa | 474 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 3.32 GPa | 482 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.440 J/cm | 0.824 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.24 J/cm | 9.82 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m² | 17.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.41 | 0.41 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.35 | 0.35 | ASTM D3702 Modified |
| K (wear) Factor | 34.2 x 10-8 mm³/N-M | 17.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 66.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 76.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 249 °C @Thickness 3.20 mm |
480 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C | 241 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 144 °C @Thickness 3.20 mm |
291 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPC TS8030 Polypropylene Copolymer, Mineral Reinforced
- Sharadaa Ceramics PCF90 (L) Precast Prefired Brick
- Struktol V-MAT G Processing Additive, Matting Agent
- Styron DL 240NA Carboxylated SB
- Universal Wire Works BNi-5 (AMS 4782) Nickel Base Brazing Filler Metal
- Westlake MC2004 High Density Polyethylene Coating
- Dow Corning Q2-5220 Resin Modifier
- Hippe PF CP 206 Cellulose Paper Reinforced Phenolic Resin - Sheet
- 3M Scotchcal™ 50-76 Graphic Film
- Bulk Molding Compounds BMC T60-6006 Wear Resistant Molding Compound
Copyright © lookpolymers.com All Rights Reserved