SABIC Innovative Plastics LNP LUBRICOMP RL0049S PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RL0049S PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* RL0049S is a compound based on Nylon 66 resin containing 20% PTFE. Added features of this material include: Flame Retardant, Heat Stabilized, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.380 % | 0.380 % | 50% RH, 24 hrs; ASTM D570 |
| 0.550 % | 0.550 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm @Time 86400 sec |
0.015 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0152 cm/cm @Time 86400 sec |
0.0152 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0167 cm/cm @Time 86400 sec |
0.0167 in/in @Time 24.0 hour |
ISO 294 |
| 0.017 cm/cm @Time 86400 sec |
0.017 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | ISO 527 |
| 47.0 MPa | 6820 psi | ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| 2.2 % | 2.2 % | ASTM D638 | |
| Tensile Modulus | 3.16 GPa | 458 ksi | 1 mm/min; ISO 527 |
| 3.17 GPa | 460 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 77.0 MPa | 11200 psi | ASTM D790 |
| 78.0 MPa | 11300 psi | ISO 178 | |
| Flexural Modulus | 2.97 GPa | 431 ksi | ISO 178 |
| 3.09 GPa | 448 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.210 J/cm | 0.393 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.70 J/cm | 3.18 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 95.0 °C @Thickness 3.20 mm |
203 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics GELOY CR8510 ASA (Asia Pacific)
- PolyOne Geon™ L4605 Red 7640 Polyvinyl Chloride, Semi-Rigid (PVC, Semi-Rigid)
- Menzolit Menzolit® SMC 0600 Unsaturated Polyester UP
- SABIC Innovative Plastics Valox® 310SE0 PBT
- Westlake EF601 Low Density Polyethylene
- Wolf Kunststoff ZEDEX® ZX-750V5KF 055 Polymer Alloy. Fiber Reinforced
- Tra-Con Tra-Duct 2705 Room Temperature Conductive Nickel Epoxy Adhesive
- Teknor Apex Telcar® TL-97-T0214B-55 Thermoplastic Elastomer
- Teknor Apex Sarlink® 4439D Thermoplastic Elastomer
- SMAC CABLE® 25235-10-08 Damping Material
Copyright © lookpolymers.com All Rights Reserved