SABIC Innovative Plastics LNP LUBRICOMP RFL36S PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP RFL36S PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* RFL36S is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Heat Stabilized.
Physical Properties Metric English Comments
Density 1.51 g/cc
0.0546 lb/in³
ASTM D792
Mechanical Properties Metric English Comments
Tensile Strength at Break 138 MPa
20000 psi
ISO 527
139 MPa
20200 psi
ASTM D638
Elongation at Break 2.1 %
2.1 %
ASTM D638
2.1 %
2.1 %
ISO 527
Flexural Strength 211 MPa
30600 psi
ISO 178
236 MPa
34200 psi
ASTM D790
Flexural Modulus 9.70 GPa
1410 ksi
ISO 178
Dart Drop, Total Energy 10.0 J
7.38 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.58
0.58
ASTM D3702 Modified
K (wear) Factor 24.2 x 10-8 mm³/N-M
12.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 37.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 21.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
37.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
 21.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 55.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 30.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2