SABIC Innovative Plastics LNP LUBRICOMP PFL36 PA 6 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP PFL36 PA 6 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* PFL36 is a compound based on Nylon 6 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 109 MPa | 15800 psi | ASTM D638 |
| 113 MPa | 16400 psi | ISO 527 | |
| Tensile Strength, Yield | 110 MPa | 16000 psi | ASTM D638 |
| 113 MPa | 16400 psi | ISO 527 | |
| Elongation at Break | 4.4 % | 4.4 % | ISO 527 |
| 6.7 % | 6.7 % | ASTM D638 | |
| Elongation at Yield | 4.1 % | 4.1 % | ISO 527 |
| 5.8 % | 5.8 % | ASTM D638 | |
| Tensile Modulus | 7.88 GPa | 1140 ksi | 1 mm/min; ISO 527 |
| 8.27 GPa | 1200 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 172 MPa | 24900 psi | ISO 178 |
| Flexural Modulus | 5.51 GPa | 799 ksi | ASTM D790 |
| 7.00 GPa | 1020 ksi | ISO 178 | |
| Izod Impact, Notched | 1.49 J/cm | 2.79 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.89 J/cm | 20.40 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 79.0 kJ/m² | 37.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 19.0 J | 14.0 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 216 °C @Thickness 3.20 mm |
421 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 396 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 201 °C @Thickness 3.20 mm |
394 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene Latice® 5587 Carboxylated Styrene - Butadiene Copolymer
- PolyOne Geon™ Vinyl Flexible R157AE Polyvinyl Chloride, Flexible (PVC, Flexible)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR Hi-Sil 233 Filler
- Covestro Apec® DP9-9333 High-Heat Polycarbonate, General Purpose, UV-Stabilized (discontinued **)
- Techmer ES HiFill® PA6 CM40 HS 40% Mineral Filled
- Sika Industry SikaFlex 255FC Fast Cure One Part Polyurethane Adhesive
- Teknor Apex APEX® 80851 Polyvinyl Chloride, Flexible
- ExxonMobil Bicor® 84 AOH OPP Film
- ExxonMobil EXACT™ 8230 Plastomer for Polymer Modification
Copyright © lookpolymers.com All Rights Reserved