SABIC Innovative Plastics LNP LUBRICOMP OFL36A PPS - Branched
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP OFL36A PPS - Branched.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* OFL36A is a compound based on PPS - Branched resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.69 g/cc | 0.0611 lb/in³ | ASTM D792 |
| 1.69 g/cc | 0.0611 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0400 % | 0.0400 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm @Time 86400 sec |
0.0010 - 0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0013 - 0.0018 cm/cm @Time 86400 sec |
0.0013 - 0.0018 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0048 cm/cm @Time 86400 sec |
0.0030 - 0.0048 in/in @Time 24.0 hour |
ISO 294 |
| 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 124 MPa | 18000 psi | ISO 527 |
| 144 MPa | 20900 psi | ASTM D638 | |
| Elongation at Break | 1.4 % | 1.4 % | ISO 527 |
| 1.7 % | 1.7 % | ASTM D638 | |
| Tensile Modulus | 11.1 GPa | 1610 ksi | 1 mm/min; ISO 527 |
| 12.34 GPa | 1790 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 197 MPa | 28600 psi | ISO 178 |
| 199 MPa | 28900 psi | ASTM D790 | |
| Flexural Modulus | 10.95 GPa | 1588 ksi | ISO 178 |
| 11.03 GPa | 1600 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.50 J/cm | 10.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² | 12.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J | 2.21 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.44 | 0.44 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.35 | 0.35 | ASTM D3702 Modified |
| K (wear) Factor | 66.5 x 10-8 mm³/N-M | 33.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 23.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 48.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 50.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 266 °C | 511 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 268 °C @Thickness 3.20 mm |
514 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Quadrant EPP Ketron® CA30 PEEK + carbon fibres, extruded (ISO Data)
- BP Amoco Innovene 1088 Polypropylene Homopolymer (discontinued **)
- Michelman® VaporCoat® 1500
- Materion BrushCAST® 20CT Fine Grain Casting Alloy (As Cast)
- Karina 40/14-FC-LMP Green Color Concentrate for PVC
- SABIC Innovative Plastics LNP LUBRICOMP RFL33 PA 66 (Europe-Africa-Middle East)
- Solvay RHODACAL® SS-35/A Surfactant
- Eagle Brass 19210 XP-10 Copper Iron, Spring
- ChevronTexaco Delo® 400 SAE 40
Copyright © lookpolymers.com All Rights Reserved