SABIC Innovative Plastics LNP LUBRICOMP OCP34E PPS - Linear (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP OCP34E PPS - Linear (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* OCP34E is a compound based on PPS - Linear resin containing Silicone, Carbon Fiber, PTFE. Added features of this material include: Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ASTM D792 |
| 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.00080 cm/cm @Time 86400 sec |
0.00080 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0039 cm/cm @Time 86400 sec |
0.0039 in/in @Time 24.0 hour |
ISO 294 |
| 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 159 MPa | 23100 psi | ISO 527 |
| 164 MPa | 23800 psi | ASTM D638 | |
| Elongation at Break | 1.3 % | 1.3 % | ISO 527 |
| 1.6 % | 1.6 % | ASTM D638 | |
| Tensile Modulus | 16.59 GPa | 2406 ksi | 1 mm/min; ISO 527 |
| 18.96 GPa | 2750 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 231 MPa | 33500 psi | ASTM D790 |
| 236 MPa | 34200 psi | ISO 178 | |
| Flexural Modulus | 14.96 GPa | 2170 ksi | ASTM D790 |
| 15.32 GPa | 2222 ksi | ISO 178 | |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.89 J/cm | 7.29 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 4.00 J | 2.95 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 265 °C @Thickness 3.20 mm |
509 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Parker Chomerics MESH STRIP™ (all metal) Wire Mesh EMI Gasket Selection Guide
- SABIC Innovative Plastics Lexan® FXD124R PC (Europe-Africa-Middle East)
- LNP Thermocomp® EC-1006 Polyetherimide, Carbon Fiber Reinforcement (discontinued **)
- KKPC Kuhmo HF 430U Weather-resistant Flame Retarded HIPS
- Shakespeare MX-229 PVDF Monofilament
- DuPont Performance Polymers Delrin® FG500P NC010 Acetal (POM) (Unverified Data**)
- AK Steel Hot Rolled Carbon Steel, Drawing Steel with Boron (DS Type B), Standard Grade
- Axiall 8630 Moldings & Extrusions Flexible PVC
- Henkel Turco 6813 E Paint Remover
Copyright © lookpolymers.com All Rights Reserved