SABIC Innovative Plastics LNP LUBRICOMP OCL36XXP PPS - Linear (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP OCL36XXP PPS - Linear (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* OCL36XXP is a compound based on PPS- Linear resin containing PTFE, Carbon Fiber. Added features include : Internally Lubricated, Electrically Conductive .
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0010 cm/cm @Time 86400 sec |
0.00050 - 0.0010 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0035 - 0.0040 cm/cm @Time 86400 sec |
0.0035 - 0.0040 in/in @Time 24.0 hour |
ISO 294 |
| Melt Index of Compound | 8.0 g/10 min @Load 5.00 kg, Temperature 315 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 599 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 163 MPa | 23600 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 0.80 % | 0.80 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 24.9 GPa | 3610 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 219 MPa | 31800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 21.3 GPa | 3090 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.39 | 0.39 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.34 | 0.34 | ASTM D3702 Modified |
| K (wear) Factor | 38.3 x 10-8 mm³/N-M | 19.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 3.00 µm/m-°C @Temperature 23.0 - 60.0 °C |
1.67 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
30.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10 - 1000 ohm | 10 - 1000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Honeywell Capran® NyLid™ OMBS-100M Nylon Lidding Film (discontinued **)
- FKuR Kunststoff Bio-Flex® F 2110 Compostable PLA Blend
- Haynes 214® alloy, sheet, 32 hours exposure at 760°C (1400°F)
- Latrobe Lescalloy® 13-8 Mo VIM-VAR Precipitation Hardening Stainless Steel
- Solvay TECHNYL® C 216 V45 PA6, 45% glass fiber, Conditioned
- Techmer ES HiFill® PA6 GF50 RM LE 50% Glass Filled (Dry)
- SSAB Tunnplat Dogal 420YP High-strength Metal-coated Steel
- Stir SpA Giesse EPM/60 (PVC)
- Cosmic Plastics K61 Long Glass Fiber Filled Iso Diallyl Phthalate Molding Compound
- Polyram PlusTek RA320G5 Nylon 66 for Injection Molding, 25% Glass-Fiber Reinforced, Flame Retardant and High Stiffness
Copyright © lookpolymers.com All Rights Reserved