SABIC Innovative Plastics LNP LUBRICOMP 9X98026 PA 46 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 46 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP 9X98026 PA 46 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* 9X98026 is a compound based on PA4.6 resin containing Barium Sulfate, PTFE and Carbon Fiber
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.11 g/cc | 0.0762 lb/in³ | ISO 1183 |
| Water Absorption | 1.6 % @Time 86400 sec |
1.6 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 159 MPa | 23100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.2 % | 1.2 % | 5 mm/min; ISO 527 |
| 1.8 % | 1.8 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Tensile Modulus | 19.3 GPa | 2800 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 207 MPa | 30000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 14.2 GPa | 2060 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 12.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
6.67 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 58.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
32.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 289 °C | 552 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 281 °C | 538 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- RheTech Products T40P109-01 40% Talc Reinforced Polypropylene, Black
- PolyOne Versaflex™ OM 6059-9 Thermoplastic Elastomer (TPE)
- Polymax® Maxelast® P3850H TPE, PP Overmold or Standalone use
- SABIC Innovative Plastics Lexan® EXL1112 PC Copolymer (Europe-Africa-Middle East)
- NanoAmor 94%, OD/WT/L: 20-50/1-2 nm/0.5-2 um Multi-Walled Carbon Nanotubes
- Kraton® G1645 M (SEBS) Linear Triblock Copolymer
- Grupo Repol Dinalon® B1S25 B30 PA6 30% Glass Beads
- Techmer ES Elastoblend® POM CO IM MB
- Samsung Cheil Industries Starex® GR-4030 ABS, 30% Glass Filled
- Elastomer Engineering E558 Polyurethane
Copyright © lookpolymers.com All Rights Reserved