SABIC Innovative Plastics LNP KONDUIT OX11314 PPS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Konduit |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP KONDUIT OX11314 PPS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Thermally conductive mineral and glass fiber filled PPS Eco-FR compound
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.91 g/cc | 0.0690 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0026 cm/cm | 0.0026 in/in | on Tensile Bar; SABIC Method |
| 0.0039 cm/cm @Time 86400 sec |
0.0039 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0041 cm/cm @Time 86400 sec |
0.0041 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 0.50 % | 0.50 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 15.0 GPa | 2180 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 75.0 MPa | 10900 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 15.5 GPa | 2250 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
11.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 21.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
11.7 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 | |
| 22.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
12.2 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 30.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 32.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
17.8 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 | |
| 35.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
19.4 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Thermal Conductivity | 0.750 W/m-K | 5.20 BTU-in/hr-ft²-°F | through-plane, ø80*3mm discs; ISO 22007-2 |
| 1.95 W/m-K | 13.5 BTU-in/hr-ft²-°F | in-plane, ø80*3mm discs; ISO 22007-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 261 °C | 502 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C | 412 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 254 °C | 489 °F | Rate B/120; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 60 - 120 arcs | 60 - 120 arcs | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Quadrant EPP TIVAR® 1000 UV Stabilized UHMW-PE, Natural & Colored Except Black (ASTM Product Data Sheet)
- Carmel Olefins IPETHENE® 214 Low Density Polyethylene (discontinued **)
- LyondellBasell Microthene® G MN71400 Low Density Polyethylene
- LyondellBasell Petrothene® NA951000 Low Density Polyethylene
- SABIC Innovative Plastics NORYL WCP821 PPE-TPE (Europe-Africa-Middle East)
- Supreme Petrochem SC 201LV General Purpose Polystyrene
- DuPont Teijin Films Mylar® OB13AF Polyester Film, 150 Gauge
- Trelleborg Emerson & Cuming Stycast® 4640-25 Two-Component Silicone Flexible Encapsulant
- Lubrizol ESTANE® ETE60DT3 Ester Based Thermoplastic Polyurethane (European Grade)