SABIC 726 Series Linear Low Density Polyethylene for Blown Film

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer	SABIC
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC 726 Series Linear Low Density Polyethylene for Blown Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: 726 series resins are fractional index Linear Low Density Polyethylene grades suitable for blown film applications. Films produced using these resins give a relatively higher stiffness, good tensile properties, impact strength and sealing properties.726N: No Slip & No Antiblock726Q: 1250 ppm Slip & 750 ppm AntiblockTypical Applications: Bread bags, textile and garment packaging, shipping sacks, can liners, carrier bags, etc.Information provided by SABIC.

Physical Properties	Metric	English	Comments
Density	0.926 g/cc	0.0335 lb/in³	load density; ASTM D1505
Thickness	30.0 microns	1.18 mil
Melt Flow	0.70 g/10 min @Load 2.16 kg, Temperature 190 °C	0.70 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	13.0 MPa	1890 psi	ASTM D882
Film Tensile Strength at Yield, TD	12.0 MPa	1740 psi	ASTM D882
Film Elongation at Break, MD	600 %	600 %	ASTM D882
Film Elongation at Break, TD	750 %	750 %	ASTM D882
Elmendorf Tear Strength MD	85 g	85 g	ASTM D1922
Elmendorf Tear Strength TD	250 g	250 g	ASTM D1922
Elmendorf Tear Strength, MD	2.83 g/micron	71.9 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	8.33 g/micron	212 g/mil	ASTM D1922
Dart Drop Total Energy	620 J/cm	1.16 ft-lb/mil	Puncture Resistance; SABIC Method
Dart Drop	2.83 g/micron	71.9 g/mil	ASTM D1709
Dart Drop Test	85.0 g	0.187 lb	ASTM D1709
Film Tensile Strength at Break, MD	42.0 MPa	6090 psi	ASTM D882
Film Tensile Strength at Break, TD	36.0 MPa	5220 psi	ASTM D882
1% Secant Modulus, MD	300 MPa	43500 psi	ASTM D882
1% Secant Modulus, TD	320 MPa	46400 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Vicat Softening Point	105 °C	221 °F	ASTM D1525

Optical Properties	Metric	English	Comments
Haze	13 %	13 %	ASTM D1003
Gloss	75 %	75 %	at 45°; ASTM D2457

Processing Properties	Metric	English	Comments
Melt Temperature	195 - 225 °C	383 - 437 °F
Blow-up Ratio (BUR)	2.0 - 3.0	2.0 - 3.0