PolyOne Geon™ Vinyl Wire & Cable WEMB410 Polyvinyl Chloride, Flexible (PVC, Flexible)

Category	Polymer , Thermoplastic , Vinyl (PVC) , PVC, Wire and Cable Grade
Manufacturer	PolyOne Corporation
Trade Name	Geon™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Geon™ Vinyl Wire & Cable WEMB410 Polyvinyl Chloride, Flexible (PVC, Flexible).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.32 g/cc	1.32 g/cc	ASTM D792

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	91	91	15 sec; ASTM D2240
Hardness, Shore D	38	38	15 sec; ASTM D2240
Tensile Strength, Yield	20.7 MPa	3000 psi	Type IV, 510 mm/min; ASTM D638
Elongation at Break	300 %	300 %	Type IV, 510 mm/min; ASTM D638

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	105 °C	221 °F	UL Temperature Rating
Brittleness Temperature	-22.0 °C	-7.60 °F	ASTM D746
Oxygen Index	31 % @Thickness 3.18 mm	31 % @Thickness 0.125 in	ASTM D2863

Electrical Properties	Metric	English	Comments
Volume Resistivity	5.60e+15 ohm-cm	5.60e+15 ohm-cm	ASTM D257

Processing Properties	Metric	English	Comments
Melt Temperature	177 - 188 °C	351 - 370 °F

Descriptive Properties	Value	Comments
Agency Ratings	UL I Oil Rating
	UL QMTT2
	UL VW-1
Features	Flame Retardant
Forms	Pellets
Generic Material	PVC, Flexible
Generic Name	Polyvinyl Chloride, Flexible (PVC, Flexible)
Processing Method	Extrusion
	Extrusion Coating
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Retention of Tensile Elongation	90%	136°C, 762.0 µm; 168 hr, UL Standard
Retention of Tensile Strength	110%	136°C, 762.0 µm; 168 hr, UL Standard
RoHS Compliance	RoHS Compliant
Uses	Building Wire Insulation
	Insulation
	Wet Rated Insulation
	Wire & Cable Applications
Wire Types	THHN
	THHW
	THW
	THW-2
	THWN
	THWN-2
	TW