Rogers Corporation Poron® 4790-79SP-15012 Urethane Shock Pad Foam

Category Polymer , Thermoset , Polyurethane, TS , Thermoset Polyurethane Foam, Unreinforced
Manufacturer Rogers Corporation
Trade Name Poron®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Rogers Corporation Poron® 4790-79SP-15012 Urethane Shock Pad Foam.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Rogers Corporation.
Physical Properties Metric English Comments
Density 0.240 g/cc
0.00868 lb/in³
ASTM D3574-95 Test A
Thickness 27.9 - 43.2 microns
1.10 - 1.70 mil
Supported Adhesive
191 - 343 microns
7.50 - 13.5 mil
Urethane Foam
229 - 381 microns
9.00 - 15.0 mil
Total Construction
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 78 %
78 %
ASTM D882
74 %

@Temperature 66.0 °C,
Time 346000 sec
 74 %

@Temperature 151 °F,
Time 96.0 hour
 80% RH; ASTM D882
Film Elongation at Break, TD 32 %
32 %
ASTM D882
66 %

@Temperature 66.0 °C,
Time 346000 sec
 66 %

@Temperature 151 °F,
Time 96.0 hour
 80% RH; ASTM D882
Compressive Yield Strength 0.0299 MPa

@Strain 25.0 %
 4.34 psi

@Strain 25.0 %
 0.2"/min. strain rate
Tear Strength 0.310 kN/m

@Time 1190 sec
 1.77 pli

@Time 0.330 hour
 Peel Adhesion, 180° Peel, to Polypropylene; ASTM D1000
0.320 kN/m

@Time 1190 sec
 1.83 pli

@Time 0.330 hour
 Peel Adhesion, 180° Peel, to Stainless Steel; ASTM D1000
0.320 kN/m

@Time 259000 sec
 1.83 pli

@Time 72.0 hour
 Peel Adhesion, 180° Peel, to Polypropylene; ASTM D1000
0.330 kN/m

@Time 1190 sec
 1.88 pli

@Time 0.330 hour
 Peel Adhesion, 180° Peel, to ABS; ASTM D1000
0.330 kN/m

@Time 1190 sec
 1.88 pli

@Time 0.330 hour
 Peel Adhesion, 180° Peel, to Acrylic; ASTM D1000
0.340 kN/m

@Time 1190 sec
 1.94 pli

@Time 0.330 hour
 Peel Adhesion, 180° Peel, to Polycarbonate; ASTM D1000
0.360 kN/m

@Time 259000 sec
 2.05 pli

@Time 72.0 hour
 Peel Adhesion, 180° Peel, to Stainless Steel; ASTM D1000
0.390 kN/m

@Time 259000 sec
 2.23 pli

@Time 72.0 hour
 Peel Adhesion, 180° Peel, to ABS; ASTM D1000
0.390 kN/m

@Time 259000 sec
 2.23 pli

@Time 72.0 hour
 Peel Adhesion, 180° Peel, to Acrylic; ASTM D1000
0.404 kN/m

@Time 259000 sec
 2.31 pli

@Time 72.0 hour
 Peel Adhesion, 180° Peel, to Polycarbonate; ASTM D1000
Compression Set 2.0 %

@Temperature 70.0 °C
 2.0 %

@Temperature 158 °F
 ASTM D3584-95
<= 10 %

@Temperature 70.0 °C
 <= 10 %

@Temperature 158 °F
 ASTM D3584-95
Seal Strength 9.40 g/25 mm
9.40 g/in
Release Adhesion, 180° Peel; ASTM D1000
10.6 g/25 mm

@Temperature 66.0 °C,
Time 346000 sec
 10.6 g/in

@Temperature 151 °F,
Time 96.0 hour
 Release Adhesion, 180° Peel, 80% RH; ASTM D1000
Descriptive Properties Value Comments
Tack 411 g
ASTM D2979 (1 second dwell), 96 hours at 66°C/80% RH
424 g
ASTM D2979 (1 second dwell)
Tensile, CMD (lb) per ASTM D882 5
80% RH; 66°C; 96 hr
9.1
Tensile, MD (lb) per ASTM D882 11.4
80% RH; 66°C; 96 hr
12
Users viewing this material also viewed the following: