- Qualchem Danaprop PP1GF-30 Polypropylene, 30% Glass Fiber
Qualchem Danaprop PP1GF-30 Polypropylene, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Qualchem Zrt. |
| Trade Name | Danaprop |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Qualchem Danaprop PP1GF-30 Polypropylene, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polypropylene (co-polymer) reinforced with glass fiberInformation provided by Qualchem Zrt.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Filler Content | 28 - 32 % | 28 - 32 % | |
| Linear Mold Shrinkage | 0.0016 cm/cm | 0.0016 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238L |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 96.0 MPa | 13900 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 4.5 % | 4.5 % | ASTM D638 |
| Tensile Modulus | 7.79 GPa | 1130 ksi | ASTM D638 |
| Flexural Strength | 135 MPa | 19600 psi | 10mm/min; ASTM D790 |
| Flexural Modulus | 5.70 GPa | 827 ksi | ASTM D790 |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 80-8387 Polyacetal-copolymer, unreinforced
- Isoflon Virgin PTFE Polytetrafluoroethylene
- KYDEX® FST Fully Compliant Aviation Thermoforming Sheet
- Taiwan Sheen Soon Sheenthane® A8630F Thermoplastic Polyurethane Elastomer
- DuPont Elvanol® 52-22 Polyvinyl Alcohol Partially Hydrolyzed General Purpose Grade
- Hexcel® AS4 Carbon Fiber (6000 Filaments)
- Arlon LW201C##FR-P0 Silicone Rubber
- Radici Heraflex® P46D 11 I RB T 200 Modified Polypropylene
Copyright © lookpolymers.com All Rights Reserved