Quadrant EPP Fluorosint® HPV Mica-filled PTFE (ASTM Product Data Sheet)
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE |
| Manufacturer | Quadrant Engineering Plastics Products |
| Trade Name | Fluorosint® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Quadrant EPP Fluorosint® HPV Mica-filled PTFE (ASTM Product Data Sheet).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.06 g/cc | 2.06 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | Immersion, 24hr; ASTM D570(2) |
| Water Absorption at Saturation | 0.43 % | 0.43 % | Immersion; ASTM D570(2) |
| Deformation | 3.2 % | 3.2 % | 2000 psi; 122°F (50°C) |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 44 | 44 | ASTM D785 |
| Hardness, Shore D | 61 | 61 | ASTM D2240 |
| Tensile Strength | 10.0 MPa | 1450 psi | ASTM D638 |
| Elongation at Break | 65 % | 65 % | ASTM D638 |
| Tensile Modulus | 1.45 GPa | 210 ksi | ASTM D638 |
| Flexural Strength | 17.2 MPa | 2500 psi | ASTM D790 |
| Flexural Modulus | 1.14 GPa | 165 ksi | ASTM D790 |
| Compressive Strength | 20.7 MPa | 3000 psi | 10% Def.; ASTM D695 |
| Compressive Modulus | 0.758 GPa | 110 ksi | ASTM D695 |
| Shear Strength | 17.2 MPa | 2500 psi | ASTM D732 |
| Izod Impact, Notched | 0.961 J/cm | 1.80 ft-lb/in | ASTM D256 Type A |
| Coefficient of Friction, Dynamic | 0.15 | 0.15 | Dry vs. Steel; QTM 55007 |
| K (wear) Factor | 76.5 x 10-8 mm³/N-M | 38.0 x 10-10 in³-min/ft-lb-hr | QTM 55010 |
| Limiting Pressure Velocity | 0.7006 MPa-m/sec | 20000 psi-ft/min | 4:1 safety factor; QTM 55007 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 88.2 µm/m-°C @Temperature -40.0 - 149 °C |
49.0 µin/in-°F @Temperature -40.0 - 300 °F |
ASTM E831 |
| Melting Point | 327 °C | 621 °F | Crystalline, Peak; ASTM D3418 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Long Term |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | 1/8 inch (Estimated Rating) |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistivity per Square | >= 1.00e+13 ohm | >= 1.00e+13 ohm | EOS/ESD S11.11 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| 3A-Dairy | No | No | |
| Canada AG | No | No | |
| FDA | Yes | Yes | |
| NSF | No | No | |
| USDA | No | No | |
| USP Class VI | No | No |
| Chemical Resistance Properties | Metric | English | Comments |
|---|---|---|---|
| Acids, Strong (pH 1-3) | Acceptable | Acceptable | |
| Acids, Weak | Acceptable | Acceptable | |
| Alcohols | Acceptable | Acceptable | |
| Alkalies, Strong (pH 11-14) | Unacceptable | Unacceptable | |
| Alkalies, Weak | Acceptable | Acceptable | |
| Chlorinated Solvents | Acceptable | Acceptable | |
| Conductive / Static Dissipative | No | No | |
| Continuous Sunlight | Acceptable | Acceptable | |
| Hot Water / Steam | Limited | Limited | |
| Hydrocarbons - Aliphatic | Acceptable | Acceptable | |
| Hydrocarbons - Aromatic | Acceptable | Acceptable | |
| Inorganic Salt Solutions | Acceptable | Acceptable | |
| Ketones, Esters | Acceptable | Acceptable |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Machinability | 2 | 1-10, 1=Easier to Machine |
Users viewing this material also viewed the following:
- Nye Lubricants PG-1S Grease
- Radici Heraflex® E 7722 TPC-ET Thermoplastic Elastomer
- RedEye On Demand VeroBlue PolyJet™ FC840 for Rapid Prototyping
- Overview of materials for Polyphthalamide (PPA), Carbon Fiber
- Solvay Specialty Polymers Catalyst CT/7-LR UV Polyolefin
- Loctite® 3607 Pin Transfer
- EMS-Grivory Grivory® BK-50 PA6-GB50
- ExxonMobil LLP8555.25 Rotational Molding Resin
- Beijing Ranger Chem BLUESTAR® BS450 Acetal Copolymer
Copyright © lookpolymers.com All Rights Reserved