Quadrant EPP Cestilene™ HD 1000 R Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded |
| Manufacturer | Quadrant Engineering Plastics Products |
| Trade Name | Cestilene™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Quadrant EPP Cestilene™ HD 1000 R Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Quadrant Engineering Plastic Products for polymers in their European product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ISO 1183 |
| Water Absorption | 0.010 % | 0.010 % | immersion |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 61 | 61 | after 15 sec.; ISO 868 |
| 63 | 63 | after 3 sec.; ISO 868 | |
| Ball Indentation Hardness | 40.0 MPa | 5800 psi | ISO 2039-1 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ISO 527 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527 |
| Elongation at Yield | 13 % | 13 % | ISO 527 |
| Tensile Modulus | 0.950 GPa | 138 ksi | ISO 527 |
| Compressive Yield Strength | 6.00 MPa | 870 psi | at 1% nominal strain; ISO 604 |
| 10.5 MPa | 1520 psi | at 2% nominal strain; ISO 604 | |
| 18.0 MPa | 2610 psi | at 5% nominal strain; ISO 604 | |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | >= 9.00 J/cm² | >= 42.8 ft-lb/in² | Partial Break; ISO 179/1eA |
| Abrasion | 180 | 180 | Relative loss per DSM internal test (CESTILENE HD 1000 = 100) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 175 - 225 µm/m-°C @Temperature 20.0 °C |
97.2 - 125 µin/in-°F @Temperature 68.0 °F |
|
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | |
| Melting Point | 130 - 135 °C | 266 - 275 °F | ISO 3146; DSC, 10°C/min |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | 20,000 hours continuous |
| 120 °C | 248 °F | for short periods | |
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ISO 75 method A |
| Vicat Softening Point | 80.0 °C | 176 °F | ISO 306 |
| Minimum Service Temperature, Air | -150 °C | -238 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Oxygen Index | <= 20 % | <= 20 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 93 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 93 |
| Dielectric Constant | 2.1 @Frequency 100 Hz |
2.1 @Frequency 100 Hz |
IEC 250 |
| 2.9 @Frequency 1e+6 Hz |
2.9 @Frequency 1e+6 Hz |
IEC 250 | |
| Dielectric Strength | <= 45.0 kV/mm | <= 1140 kV/in | IEC 243 |
| Dissipation Factor | 0.00040 @Frequency 100 Hz |
0.00040 @Frequency 100 Hz |
IEC 250 |
| 0.00080 @Frequency 1e+6 Hz |
0.00080 @Frequency 1e+6 Hz |
IEC 250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | green |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Amodel® AS-1145 HS Polyphthalamide (PPA), 45% Glass Fiber (Dry)
- Shin-Etsu Silicones KE-561U Silicone Elastomer
- A. Schulman POLYFORT™ FPP 3063UV-3120 Black, UV Stabilized Modified Polypropylene
- Hexcel® HexWeb® CR III 1/4-5052-.003 Corrosion Resistant Specification Grade Aluminum Honeycomb
- Cossa Polimeri ESTABLEND PA 6000 ABS / Nylon 6 Blend
- Eastman Tritan MX730 Copolyester
- BASF Lucalen® A 3110 M Q 244 Ethylene/Acrylate Copolymer
- Aremco Aremco-Bond™ 570 High Performance Epoxide
Copyright © lookpolymers.com All Rights Reserved