Quadrant EPP Acetron® POM-C Copolymer Acetal, Porosity-Free, Unfilled, Extruded
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Quadrant Engineering Plastics Products |
| Trade Name | Acetron® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Quadrant EPP Acetron® POM-C Copolymer Acetal, Porosity-Free, Unfilled, Extruded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | Immersion, 24hr; ASTM D570(2) |
| Water Absorption at Saturation | 0.90 % | 0.90 % | Immersion; ASTM D570(2) |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 88 | 88 | ASTM D785 |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Hardness, Shore D | 85 | 85 | ASTM D2240 |
| Tensile Strength | 65.5 MPa | 9500 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Tensile Modulus | 2.76 GPa | 400 ksi | ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Compressive Strength | 103 MPa | 15000 psi | 10% Def.; ASTM D695 |
| Compressive Modulus | 2.76 GPa | 400 ksi | ASTM D695 |
| Shear Strength | 55.2 MPa | 8000 psi | ASTM D732 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 Type A |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | Dry vs. Steel; QTM55007 |
| K (wear) Factor | 403 x 10-8 mm³/N-M | 200 x 10-10 in³-min/ft-lb-hr | QTM 55010 |
| Limiting Pressure Velocity | 0.0946 MPa-m/sec | 2700 psi-ft/min | 4:1 safety factor; QTM 55007 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 97.2 µm/m-°C @Temperature -40.0 - 149 °C |
54.0 µin/in-°F @Temperature -40.0 - 300 °F |
ASTM E831 |
| Thermal Conductivity | 0.231 W/m-K | 1.60 BTU-in/hr-ft²-°F | ASTM F433 |
| Melting Point | 168 °C | 335 °F | Crystalline, Peak; ASTM D3418 |
| Maximum Service Temperature, Air | 82.2 °C | 180 °F | Long Term |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 1/8 inch (Estimated Rating) |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistivity per Square | >= 1.00e+13 ohm | >= 1.00e+13 ohm | EOS/ESD S11.11 |
| Dielectric Constant | 3.8 @Frequency 1e+6 Hz |
3.8 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 16.5 kV/mm | 420 kV/in | Short Term; ASTM D149 |
| Dissipation Factor | 0.0050 @Frequency 1e+6 Hz |
0.0050 @Frequency 1e+6 Hz |
ASTM D150 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| 3A-Dairy | Yes | Yes | |
| Canada AG | Yes | Yes | |
| FDA | Yes | Yes | |
| NSF | Yes | Yes | STD 51 & 61 Natural Only |
| USDA | Yes | Yes | |
| USP Class VI | No | No |
| Chemical Resistance Properties | Metric | English | Comments |
|---|---|---|---|
| Acids, Strong (pH 1-3) | Unacceptable | Unacceptable | |
| Acids, Weak | Limited | Limited | |
| Alcohols | Acceptable | Acceptable | |
| Alkalies, Strong (pH 11-14) | Unacceptable | Unacceptable | |
| Alkalies, Weak | Acceptable | Acceptable | |
| Chlorinated Solvents | Limited | Limited | |
| Conductive / Static Dissipative | No | No | |
| Continuous Sunlight | Limited | Limited | |
| Hot Water / Steam | Limited | Limited | |
| Hydrocarbons - Aliphatic | Acceptable | Acceptable | |
| Hydrocarbons - Aromatic | Acceptable | Acceptable | |
| Inorganic Salt Solutions | Acceptable | Acceptable | |
| Ketones, Esters | Acceptable | Acceptable |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural / Black | |
| Machinability | 1 | 1-10, 1=Easier to Machine |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8981X (899XP-1) (UF) Synthetic Oil
- Polykemi AB POLYfill PP EIP16020 F PP Mineral Reinforced, Extrusion Grade, Low CLTE
- Radici Radilon® S RCV3015 (cond.) Nylon 6
- Meehanite Almanite® W4 Wear and Abrasion Resisting Cast Iron
- Techmer ES Luriblend® PA6/6 04003 Nylon 66
- Vyncolit X681 Novolac Phenolic
- Total PS CPDS 801 Flame Retardant Polystyrene
- Dow Corning Z-6042 SILANE
- Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F)
Copyright © lookpolymers.com All Rights Reserved