Polyram RamSter PE321G6 PET, 30% Glass Fiber, Flame Retardant
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 30% Glass Reinforced |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamSter PE321G6 PET, 30% Glass Fiber, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass fiber reinforced, flame retardant V-0 PET for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ISO 2577 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 280 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 536 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 125 MPa | 18100 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 11.16 GPa | 1619 ksi | ISO 527 |
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.50 kJ/m² | 4.04 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 254 °C | 489 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 224 °C | 435 °F | ISO 75 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
|
| Glow Wire Test | 960 °C | 1760 °F | GWFI; IEC 60695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering N50C Nitrile Rubber
- Oxford Polymers PC 30CF-925 Black PC, 30% Carbon Fiber Reinforced
- Samsung Cheil Industries Starex® SV-0165 U ABS, Unreinforced Extrusion Grade
- Polyram PlusTek PA303G6BK16 Nylon 6.6, 30% Glass Fiber reinforced, Heat Stabilized, Hydrolysis Resistant
- Entec Hylex® P1010L1 HB Polycarbonate
- Eurostar Staramide AG6 PA66, 30% Glass Filled, Injection Molded
- ExxonMobil HDP8760.29 Rotational Molding Resin
- China Tungsten ZP10-1 Tungsten Carbide
- 3M Controltac™ IJ380Cv3 Wrap Film with Comply™ v3 Adhesive
- BASF Ethylenediamine (EDA)
Copyright © lookpolymers.com All Rights Reserved