SABIC Innovative Plastics LNP STAT-KON DEL329XF PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DEL329XF PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DEL329XF is a compound based on Polycarbonate resin containing Carbon Fiber, Flame Retardant, PTFE. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0900 % | 0.0900 % | 50% RH, 24 hrs; ASTM D570 |
| 0.140 % | 0.140 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm @Time 86400 sec |
0.0010 - 0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0014 - 0.0019 cm/cm @Time 86400 sec |
0.0014 - 0.0019 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0050 cm/cm @Time 86400 sec |
0.0040 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0045 - 0.0052 cm/cm @Time 86400 sec |
0.0045 - 0.0052 in/in @Time 24.0 hour |
ISO 294 | |
| Melt Index of Compound | 20 g/10 min @Load 6.70 kg, Temperature 300 °C |
20 g/10 min @Load 14.8 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 91.0 MPa | 13200 psi | ASTM D638 |
| 94.0 MPa | 13600 psi | ISO 527 | |
| Elongation at Break | 1.9 % | 1.9 % | ISO 527 |
| 2.0 % | 2.0 % | ASTM D638 | |
| Tensile Modulus | 7.17 GPa | 1040 ksi | 50 mm/min; ASTM D638 |
| 7.30 GPa | 1060 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 138 MPa | 20000 psi | ASTM D790 |
| 139 MPa | 20200 psi | ISO 178 | |
| Flexural Modulus | 6.48 GPa | 940 ksi | ASTM D790 |
| 7.30 GPa | 1060 ksi | ISO 178 | |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.15 J/cm | 5.90 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 15.0 J | 11.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 24.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 24.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 41.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 41.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 143 °C @Thickness 3.20 mm |
289 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 139 °C @Thickness 3.20 mm |
282 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EX2078X PC (Europe-Africa-Middle East)
- Overview of materials for Polypropylene with 30% Talc Filler
- Gouda Vuurvast VIBRON 170 M GS (R) Dense Vibrating Refractory Castable
- Lanxess Durethan® BKV 130 H2.0 DUS008 901510 Nylon 6, Glass Fiber Reinforced, Impact Modified
- EMS-Grivory Grivory® GV XE 16102 (GVL-6H HP) PA*-GF60
- Arkema Group Rilsan® AESN P302 TL Nylon 12, Flexible Tubing Grade (Dry)
- 3M 8777 Sealing Tape
- Ametek Ultra 303L P/M Stainless Steel, Sintered from 6.0 g/cc Green Density
- A. Schulman POLYFLAM™ RPP 1021 General Purpose Copolymer Polypropylene
- Ineos H35G-00 Polypropylene Homopolymer
Copyright © lookpolymers.com All Rights Reserved