Polykemi AB SCANMID 6 B32^ E F30 Nylon 6, Glass Fiber Reinforced, Modified

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Polykemi AB
Trade Name SCANMID 6
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB SCANMID 6 B32^ E F30 Nylon 6, Glass Fiber Reinforced, Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Filler Content 30 %
30 %
±2%; Polykemi
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
With Flow; ISO 2577
0.0090 cm/cm
0.0090 in/in
Across Flow; ISO 2577
Mechanical Properties Metric English Comments
Hardness, Shore D 76

@Time 15.0 sec
 76

@Time 0.00417 hour
 ASTM D2240
Tensile Strength at Break <= 140 MPa
<= 20300 psi
ISO/R527
Elongation at Break 4.0 %
4.0 %
ISO/R527
Flexural Strength <= 210 MPa
<= 30500 psi
ISO 178
Flexural Modulus 7.50 GPa

@Temperature 23.0 °C
 1090 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 1.30 J/cm²

@Temperature -20.0 °C
 6.19 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
1.90 J/cm²

@Temperature 23.0 °C
 9.04 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
120°C/h; ISO 75/1
Vicat Softening Point >= 200 °C

@Load 5.001 kg
 >= 392 °F

@Load 11.03 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Glow Wire Test 650 °C

@Thickness 2.00 mm
 1200 °F

@Thickness 0.0787 in
 IEC 695-2-1