- Polykemi AB SCANMID 6 B11^ FX25 FR10 Nylon 6, Glass Fiber Reinforced, Flame Retardant
Polykemi AB SCANMID 6 B11^ FX25 FR10 Nylon 6, Glass Fiber Reinforced, Flame Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Polykemi AB |
| Trade Name | SCANMID 6 |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANMID 6 B11^ FX25 FR10 Nylon 6, Glass Fiber Reinforced, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 |
| Filler Content | 25 % | 25 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | With Flow; ISO 2577 |
| 0.0080 cm/cm | 0.0080 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 95.0 MPa | <= 13800 psi | ISO/R527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO/R527 |
| Flexural Strength | <= 162 MPa | <= 23500 psi | ISO 178 |
| Flexural Modulus | 6.50 GPa @Temperature 23.0 °C |
943 ksi @Temperature 73.4 °F |
ISO 178 |
| Izod Impact, Notched (ISO) | 5.50 kJ/m² @Temperature 23.0 °C |
2.62 ft-lb/in² @Temperature 73.4 °F |
ISO 180/4A |
| Charpy Impact, Notched | 0.350 J/cm² @Temperature 23.0 °C |
1.67 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | 120°C/h; ISO 75/1 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| 5VA @Thickness 1.60 mm |
5VA @Thickness 0.0630 in |
||
| Glow Wire Test | 960 °C @Thickness 1.60 mm |
1760 °F @Thickness 0.0630 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- Nylene® PA6/6 Homopolymer 132 HSL Nylon 6/6
- NCMT NanoPAC™ G2050H High Performance Polypropylene Nanocomposite
- SABIC Innovative Plastics Cycoloy® CY6310 PC+ABS (Europe-Africa-Middle East)
- IDI Composites C-103 Thermoset Polyester, Molding
- Lehmann & Voss LUVOCOM® 1/GK/30/TF/13/SI/2 Polyamide 66, with glass spheres, PTFE, lubricant modified, heat stabilized
- SABIC Innovative Plastics LNP LUBRICOMP FL004 PE (Asia Pacific)
- Techmer ES HiFill® PA6/6 GF30 L 30% Glass Filled
- Teknor Apex Uniprene® UN-7100-50D Thermoplastic Vulcanizate
- 3M 1003 SL Fire Barrier Water Tight Sealants
Copyright © lookpolymers.com All Rights Reserved