- HOME
- POLYMER SEARCH
- Thermoplastic
- Polycarbonate (PC)
- Polycarbonate/ASA Alloy, Unreinforced
- Polykemi AB SCANBLEND FS7 FR UV PC/ASA Blend, Flame-Retardant, UV Stabilized
Polykemi AB SCANBLEND FS7 FR UV PC/ASA Blend, Flame-Retardant, UV Stabilized
| Category | Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant , Polycarbonate/ASA Alloy, Unreinforced |
| Manufacturer | Polykemi AB |
| Trade Name | SCANBLEND |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANBLEND FS7 FR UV PC/ASA Blend, Flame-Retardant, UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | With Flow; ISO 2577 |
| 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 35 g/10 min @Load 5.00 kg, Temperature 260 °C |
35 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 45.0 MPa | <= 6530 psi | ISO/R527 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO/R527 |
| Flexural Strength | <= 80.0 MPa | <= 11600 psi | ISO 178 |
| Flexural Modulus | 2.40 GPa @Temperature 23.0 °C |
348 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 3.50 J/cm² @Temperature -20.0 °C |
16.7 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 120 °C @Load 5.001 kg |
248 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 135 °C @Load 1.00 kg |
275 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- Pyrotek J-1 Ropes
- ExxonMobil 636 Mobilgear 600 Series
- Wieland 1757 Wilaform Platinum
- Hexcel® Redux® 382H (0.06 psf) Film Adhesive
- Azoty Tarnow™ TARNOFORM 300 GF4 POM
- Bapolene® 213B Polyethylene, Extrusion Grade
- Akzo Nobel Expancel® 551 WU 80 Wet unexpanded microspheres
- Akro-Plastic Akromid® S3 GF 50 1 (3533) PA 6.10 Dry, 50% Glass Filled
- Techmer Lehvoss Compounds Luvotech™ J-4/35 NAT PA6/12 (discontinued **)
- Ascend Performance Materials Vydyne® R525 Nylon 66, 25% Glass Reinforced, Conditioned