BASF Ultradur B 4300 G3 BK5110 15% Glass Filled PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultradur B
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultradur B 4300 G3 BK5110 15% Glass Filled PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultradur B4300 G3 is an easy flowing 15% glass reinforced grade of PBT for injection molding. It is suitable for industrial articles requiring high rigidity, toughness and dimensional stability.
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 0.20 %
0.20 %
24 hour; ISO Test
0.40 %
0.40 %
ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C/50% R.H.; ISO 62
Viscosity Test 113 cm³/g
113 cm³/g
Viscosity number
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
ASTM Data; MD
Melt Flow 22 g/10 min

@Load 2.16 kg,
Temperature 250 °C
22 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 93.0 MPa
13500 psi
5mm/min; ISO 527
Elongation at Break 3.8 %
3.8 %
5mm/min; ISO 527
Tensile Modulus 5.70 GPa
827 ksi
1mm/min; ISO 527
Flexural Modulus 5.20 GPa
754 ksi
ISO Data
Izod Impact, Notched (ISO) 5.50 kJ/m²
2.62 ft-lb/in²
ISO Test
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Melting Point 223 °C
433 °F
10 K/min
223 °C
433 °F
ASTM Test
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
ISO 75
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
Descriptive Properties Value Comments
Color BK5110
Commercial Status Active America
Form Pellets
Impact Modified No
NSF Std. 61 Yes
Primary Processing Technique Injection Molding
Special characteristic Heat stabilized or stable to heat
Light stabilized or stable to light
Lubricant
U.V. stabilized or stable to weather