Polykemi AB POLYfill PP EIP5025 F VT2 Polypropylene, Mineral Reinforced, Extrusion grade, Low CLTE
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYfill PP EIP5025 F VT2 Polypropylene, Mineral Reinforced, Extrusion grade, Low CLTE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Filler Content | 25 % | 25 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | With Flow; ISO 2577 |
| 0.0090 - 0.011 cm/cm | 0.0090 - 0.011 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 22.0 MPa | <= 3190 psi | ISO/R527 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO/R527 |
| Flexural Strength | <= 40.0 MPa | <= 5800 psi | ISO 178 |
| Flexural Modulus | 1.90 GPa @Temperature 23.0 °C |
276 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact Unnotched | 1.20 J/cm² @Temperature -20.0 °C |
5.71 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature -20.0 °C |
2.38 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 73.0 °C @Load 5.001 kg |
163 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 149 °C @Load 1.00 kg |
300 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 750 °C @Thickness 2.00 mm |
1380 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- Hong Kun Group TBTU Pharmaceutical Intermediate
- Saint-Gobain Meldin® 5055 Thermoplastic Bearing Material
- Sumitomo Bakelite Durez® 32962 Phenolic Molding Compound, Injection Grade
- A. Schulman POLYBATCH™ White LL8000 AP Concentrate Based In LLDPE
- Diamond Polymers SAN 268 Styrene Acrylonitrile, Transparent Engineering Thermoplastic
- Eurostar Starflam PX06020 PA6, Flame Retardant, Injection Molded
- Azdel SuperLite® SL550600-100 PP Resin Matrix / 55% Glass Fiber (3 mm Molded Thickness)
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304, 30% Cold Rolled (UNS S30400)
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 420, Hardened + 538°C Temper
- ChevronTexaco Pinnacle® 460
Copyright © lookpolymers.com All Rights Reserved