PolyOne Trilliant™ HC X THC 1100 Natural Copolyester

Category Polymer , Thermoplastic , Polyester, TP
Manufacturer PolyOne Corporation
Trade Name Trilliant™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Trilliant™ HC X THC 1100 Natural Copolyester.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Trilliant™ HC high performance blends offer outstanding strength, durability and chemical resistance through the combination of Eastman Tritan™ copolyester with other various polymeric resins. Trilliant™ HC blends made with Tritan™ copolyester are available in standard grades or can be customized to meet specific performance requirements.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.16 g/cc
1.16 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0058 cm/cm

@Thickness 3.18 mm
0.0058 in/in

@Thickness 0.125 in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0030 cm/cm

@Thickness 3.18 mm
0.0030 in/in

@Thickness 0.125 in
ASTM D955
Melt Flow 22 g/10 min

@Load 5.00 kg,
Temperature 260 °C
22 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 36.5 MPa
5290 psi
Type I, 51 mm/min; ASTM D638
Tensile Strength, Yield 40.0 MPa
5800 psi
51 mm/min; ASTM D638
Elongation at Break 74 %
74 %
Type I, 51 mm/min; ASTM D638
Tensile Modulus 1.56 GPa
226 ksi
Type I, 51 mm/min; ASTM D638
Flexural Strength 72.4 MPa
10500 psi
13 mm/min; ASTM D790
Flexural Modulus 1.56 GPa
226 ksi
13 mm/min; ASTM D790
Izod Impact, Notched 9.60 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
18.0 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 71.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
39.4 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C

@Thickness 3.18 mm
203 °F

@Thickness 0.125 in
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C

@Thickness 3.18 mm
176 °F

@Thickness 0.125 in
Unannealed; ASTM D648
Descriptive Properties Value Comments
Features Good Chemical Resistance
Good Color Stability
Good Flow
Good Toughness
High Impact Resistance
Hydrolytically Stable
Medium Heat Resistance
Forms Pellets
Generic Material Copolyester
Generic Name Copolyester
Regional Availability Africa & Middle East
Europe
North America
South America
Uses Electrical Housing
Hospital Goods
Housings
Medical Appliances
Medical/Healthcare Applications
Thin-walled Parts