PolyOne Syncure™ System S117FH Polyethylene, Crosslinked (XLPE)

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer PolyOne Corporation
Trade Name Syncure™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Syncure™ System S117FH Polyethylene, Crosslinked (XLPE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
NOTE: The above represents Typical Properties measured on 20 AWG with 16 mil wall. STORAGE AND HANDLING: Use within 48 hours once package is open to avoid self-curing and scrap.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Deformation 18 %

@Temperature 131 °C,
Time 3600 sec
18 %

@Temperature 268 °F,
Time 1.00 hour
500 g; UL 1581
Mechanical Properties Metric English Comments
Hardness, Shore D 57
57
10 sec; ASTM D2240
62
62
ASTM D2240
Tensile Strength, Yield 16.5 MPa
2390 psi
Type IV, 510 mm/min; ASTM D638
Elongation at Break 400 %
400 %
Type IV, 510 mm/min; ASTM D638
Descriptive Properties Value Comments
Appearance Natural Color
Automotive Specifications SAE J1128
Catalyst Masterbatch 40%
V-0064G RoHS
Flame Test Pass
SAE J1128; 45 degree
Forms Pellets
Gel Content 60%
ASTM D2765; Crosslinked PE, Method B (NonReferee Test)
Generic Material XLPE
Generic Name Polyethylene, Crosslinked (XLPE)
Grafted Base Resin 60%
S-1075A
Processing Method Extrusion Coating
Regional Availability North America
Retention of Tensile Elongation 120%
155°C, 1.91 mm; 168 hr, UL Standard
Retention of Tensile Strength 100%
155°C, 1.91 mm; 168 hr, UL Standard
Uses Automotive Applications
Wire & Cable Applications