Lehmann & Voss LUVOCOMÂ® 1105-7194/GY PEEK, unreinforced

Category	Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer	Lehmann & Voss & Co.
Trade Name	LUVOCOM®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lehmann & Voss LUVOCOMÂ® 1105-7194/GY PEEK, unreinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceHigh chemical resistance parts, non flammable.Inherent flame resistance.Information provided by Lehmann & Voss & Co.KG

Physical Properties	Metric	English	Comments
Specific Gravity	1.31 g/cc	1.31 g/cc	ISO 1183
Water Absorption	<= 0.50 %	<= 0.50 %	23Â°C/24h
Linear Mold Shrinkage	0.010 - 0.016 cm/cm	0.010 - 0.016 in/in

Mechanical Properties	Metric	English	Comments
Tensile Stress	100 MPa	14500 psi
Elongation at Yield	5.0 %	5.0 %
	6.0 %	6.0 %	flexural
Modulus of Elasticity	4.00 GPa	580 ksi
Flexural Strength	140 MPa	20300 psi
Flexural Modulus	3.00 GPa	435 ksi

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	250 Â°C	482 Â°F
	260 Â°C	500 Â°F	short term
Flammability, UL94	V-0	V-0	not recognized by UL

Electrical Properties	Metric	English	Comments
Insulation Resistance	>= 1.00e+12 ohm	>= 1.00e+12 ohm

Processing Properties	Metric	English	Comments
Processing Temperature	390 Â°C	734 Â°F	mass temp
Nozzle Temperature	360 - 380 Â°C	680 - 716 Â°F
Zone 1	360 - 370 Â°C	680 - 698 Â°F
Zone 2	380 - 390 Â°C	716 - 734 Â°F
Zone 3	390 - 400 Â°C	734 - 752 Â°F
Mold Temperature	170 - 200 Â°C	338 - 392 Â°F
Drying Temperature	120 Â°C @Time 21600 - 28800 sec	248 Â°F @Time 6.00 - 8.00 hour	or
	150 Â°C @Time 10800 - 21600 sec	302 Â°F @Time 3.00 - 6.00 hour	Dehumidifying dryer

Descriptive Properties	Value	Comments
Color	grey