- PolyOne Stat-Tech™ RA-06CF-07GF/000 EM Polyarylsulfone - 7% Glass Fiber - 6% Carbon Fiber Reinforced - ESD Applications - Flow Enhanced Grade
PolyOne Stat-Tech™ RA-06CF-07GF/000 EM Polyarylsulfone - 7% Glass Fiber - 6% Carbon Fiber Reinforced - ESD Applications - Flow Enhanced Grade
| Category | Polymer , Thermoplastic , Polyarylsulfone (PAS) , Polyarylsulfone (PAS), Carbon Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Stat-Tech™ RA-06CF-07GF/000 EM Polyarylsulfone - 7% Glass Fiber - 6% Carbon Fiber Reinforced - ESD Applications - Flow Enhanced Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| Water Absorption | 0.38 % | 0.38 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.17 mm |
0.0020 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 98 | 98 | ASTM D785 |
| Tensile Strength, Ultimate | 124 MPa | 18000 psi | ASTM D638 |
| Elongation at Break | 3.0 - 4.0 % | 3.0 - 4.0 % | ASTM D638 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm @Thickness 6.35 mm |
1.20 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 39.6 µm/m-°C @Temperature 20.0 °C |
22.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | CTi Test V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+6 - 1.00e+10 ohm | 1.00e+6 - 1.00e+10 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 343 - 377 °C | 649 - 711 °F | Stock |
| Mold Temperature | 121 - 149 °C | 250 - 300 °F | |
| Drying Temperature | 135 °C | 275 °F |
Users viewing this material also viewed the following:
- RheTech Products HP521-01 15% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Black
- Nabaltec NABALOX® NO 625-31 Reactive Alumina
- SABIC Innovative Plastics Lexan® 144H PC (Europe-Africa-Middle East)
- Kingfa JH710 G10 Flame Retardant & 10% Glass Reinforced PC
- Kolon KOCETAL® TC701 Mineral Reinforced Acetal Resin
- Karina E 601D22/15 Crepe PVC Compound
- Techmer ES HiFill® PA12 L N MB
- Dow DOWLEX™ 2507 Linear Low Density Polyethylene, Narrow MW Distribution
- Fainplast Compounds FK 86 Flexible PVC, Insulation Lead Free
- Dow Corning 360 Medical Fluid, 1000 CST.
Copyright © lookpolymers.com All Rights Reserved