BASF Elastollan 685 AU TPUR

Category	Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade
Manufacturer	BASF
Trade Name	Elastollan
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Elastollan 685 AU TPUR.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and wear resistance, good damping characteristics and a high resilience performance.Typical Applications: Decorative parts and damping elements for the sport-shoe industry, ski tips, tubes and films.Note: Quoted results are from measurements on injection molded test platens, post tempered for 20 hours at 100°CInformation provided by BASF

Physical Properties	Metric	English	Comments
Density	1.21 g/cc	0.0437 lb/in³	ISO 1183-1-A

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	86	86	ISO 868
Tensile Strength	40.0 MPa	5800 psi	after storage in water at 80°C for 42 days; ISO 37
	50.0 MPa	7250 psi	ISO 37
	2.80 MPa @Strain 20.0 %	406 psi @Strain 20.0 %	ISO 37
	5.50 MPa @Strain 100 %	798 psi @Strain 100 %	ISO 37
Elongation at Break	600 %	600 %	ISO 37
	650 %	650 %	after storage in water at 80°C for 42 days; ISO 37
Charpy Impact, Notched	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	DIN EN ISO 179
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	DIN EN ISO 179
Tear Strength	75.0 kN/m	428 pli	DIN ISO 34-1/Bb
Abrasion	40	40	[mm<sup>3</sup>; ISO 4649
Compression Set	25 % @Temperature 23.0 °C	25 % @Temperature 73.4 °F	ISO 815
	45 % @Temperature 70.0 °C	45 % @Temperature 158 °F	ISO 815

Processing Properties	Metric	English	Comments
Processing Temperature	175 - 220 °C	347 - 428 °F	Extrusion
	175 - 230 °C	347 - 446 °F	Injection molding
Mold Temperature	20.0 - 70.0 °C	68.0 - 158 °F

Descriptive Properties	Value	Comments
Color	Transparent
Commercial Status	North America
Primary Processing Technique	Injection molding and Extrusion