PolyOne Stat-Tech™ AS-10NCF/000 ABS - 10% Nickel Coated Carbon Fiber (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Stat-Tech™ AS-10NCF/000 ABS - 10% Nickel Coated Carbon Fiber
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Water Absorption | 0.15 % @Thickness 3.17 mm |
0.15 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 48.3 MPa | 7000 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 4.14 GPa | 600 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 68.9 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 4.14 GPa | 600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.900 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 107 °C | 225 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.1 °C | 205 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.0 - 100 ohm-cm | 1.0 - 100 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1.0 - 100 ohm | 1.0 - 100 ohm | ASTM D257 |
| Shielding Effectiveness | 30 - 60 dB | 30 - 60 dB | 1,000 MHz; PolyOne Internal |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 204 - 232 °C | 400 - 450 °F | Molding |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 8832 C BLK
- MV Labs HO700 Ho(NO3)3·5H2O Holmium nitrate pentahydrate
- DuPont Performance Polymers Delrin® 500AL NC010 Acetal Homopolymer (Unverified Data**)
- Metabolix Mirelâ„¢ P1004 Injection Molding Grade PHA Bioplastic
- Gromax BFG30-EN03N1 Nylon 6 33% Glass Filled (Conditioned)
- SABIC Innovative Plastics LNP LUBRICOMP RZL36 PA 66 (Europe-Africa-Middle East)
- Teknor Apex Telcar® TL-1434A Thermoplastic Elastomer
- Solvay Specialty Polymers Amodel® AS-1945 HS Polyphthalamide (PPA) (Unverified Data**)
- Lubrizol Estane® 2102-75A Thermoplastic Polyurethane Elastomer
- Victrex® Vicote® F809 Polyetheretherketone (PEEK) Liquid Dispersion
Copyright © lookpolymers.com All Rights Reserved