PolyOne Lubri-Tech™ MP-30GF/15T Modified PPO - 30% Glass Fiber - 15% PTFE (discontinued **)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ MP-30GF/15T Modified PPO - 30% Glass Fiber - 15% PTFE
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.416 g/cc | 0.05116 lb/in³ | ASTM D792 |
| Water Absorption | 0.080 % | 0.080 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0015 cm/cm @Thickness 3.17 mm |
0.0010 - 0.0015 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 103 MPa | 14900 psi | ASTM D638 |
| Elongation at Break | 2.0 - 5.0 % | 2.0 - 5.0 % | ASTM D638 |
| Tensile Modulus | 5.90 GPa | 856 ksi | ASTM D638 |
| Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
| Flexural Modulus | 5.90 GPa | 856 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 - 1.60 J/cm @Thickness 6.35 mm |
2.49 - 3.00 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 277 - 316 °C | 531 - 601 °F | Stock |
| Mold Temperature | 121 °C | 250 °F | |
| Drying Temperature | 121 °C | 250 °F |
Users viewing this material also viewed the following:
- Kolon ELLAS K-787A Ester Based Thermoplastic Polyurethane
- LATI Laril 13 G/30-V1 PPOm, 30% Glass Fiber Reinforced, Flame Retardant
- PlastxWorld CEVIAN® SKG20 20% GF ABS
- A. Schulman POLYFORT™ FPP 1236 Glass Filled Chemically Coupled Homopolymer Polypropylene
- DuPont Teijin Films Mylar® MLBT Polyester Film, 48 Gauge
- Colorite Polymers 6511 Clear Extrusion Vinyl Compound
- Dynasol Calprene® 501 Thermoplastic Rubber SBS Dry
- 3M FM06E Indoor UL Recognized Brite Silver Polyester Label Products
Copyright © lookpolymers.com All Rights Reserved