PolyOne Geon™ Vinyl Cellular E2519 Polyvinyl Chloride, Rigid (PVC, Rigid)

Category Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade
Manufacturer PolyOne Corporation
Trade Name Geon™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Geon™ Vinyl Cellular E2519 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Note: Physical properties were measured on non-foamed profiles. Measured density of an extruded 1 thick free foamed part was 0.70 gms/cc at a 360 deg.F melt temperature.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.31 g/cc
1.31 g/cc
Cellular; ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore D 75
75
ASTM D2240
Tensile Strength, Yield 55.1 MPa
7990 psi
Type I, 5.1 mm/min; ASTM D638
Tensile Modulus 2.92 GPa
424 ksi
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 94.5 MPa
13700 psi
ASTM D790
Flexural Modulus 3.02 GPa
438 ksi
ASTM D790
Izod Impact, Notched 0.450 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
0.843 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Compression Molded; ASTM D256A
Dart Drop Total Energy 53.8 J/cm

@Temperature 23.0 °C
0.101 ft-lb/mil

@Temperature 73.4 °F
Procedure A, C.125; ASTM D4226
53.8 J/cm

@Temperature 23.0 °C
0.101 ft-lb/mil

@Temperature 73.4 °F
Procedure B, C.125; ASTM D4226
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 67.0 µm/m-°C
37.2 µin/in-°F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 79.4 °C

@Treatment Temp. 60.0 °C,
Thickness 3.18 mm
175 °F

@Treatment Temp. 140 °F,
Thickness 0.125 in
Annealed; ASTM D648
79.4 °C

@Treatment Temp. 50.0 °C,
Thickness 3.18 mm
175 °F

@Treatment Temp. 122 °F,
Thickness 0.125 in
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 75.6 °C

@Treatment Temp. 50.0 °C,
Thickness 3.18 mm
168 °F

@Treatment Temp. 122 °F,
Thickness 0.125 in
Annealed; ASTM D648
76.2 °C

@Treatment Temp. 60.0 °C,
Thickness 3.18 mm
169 °F

@Treatment Temp. 140 °F,
Thickness 0.125 in
Annealed; ASTM D648
Descriptive Properties Value Comments
Forms Cellular, Free Blow
Cellular, Inward Foam
Powder
Generic Material PVC, Rigid
Generic Name Polyvinyl Chloride, Rigid (PVC, Rigid)
Processing Method Extrusion
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Uses Consumer Applications
Cosmetics