PolyOne Geon™ HTX E1502 Polyvinyl Chloride Alloy (PVC Alloy)
| Category | Polymer , Thermoplastic , Vinyl (PVC) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ HTX E1502 Polyvinyl Chloride Alloy (PVC Alloy).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
VSI FLAMMABILITY:Burn Length (0.040 in Bar)ASTM D635 0* IN.Burn Time (0.040 in Bar) ASTM D635 0* Sec.*Extinguished before 25 MM starting ref mark.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 79 | 79 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 49.6 MPa | 7190 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.74 GPa | 397 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
| Flexural Modulus | 2.77 GPa | 402 ksi | ASTM D790 |
| Izod Impact, Notched | 0.340 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.637 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded; ASTM D256A |
| Dart Drop Total Energy | 67.6 J/cm @Temperature 23.0 °C |
0.127 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 68.9 J/cm @Temperature 23.0 °C |
0.129 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 64.0 µm/m-°C | 35.6 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 88.9 °C @Treatment Temp. 50.0 °C, Thickness 3.18 mm |
192 °F @Treatment Temp. 122 °F, Thickness 0.125 in |
Annealed; ASTM D648 |
| 90.0 °C @Treatment Temp. 60.0 °C, Thickness 3.18 mm |
194 °F @Treatment Temp. 140 °F, Thickness 0.125 in |
Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.4 °C @Treatment Temp. 50.0 °C, Thickness 3.18 mm |
184 °F @Treatment Temp. 122 °F, Thickness 0.125 in |
Annealed; ASTM D648 |
| 84.4 °C @Treatment Temp. 60.0 °C, Thickness 3.18 mm |
184 °F @Treatment Temp. 140 °F, Thickness 0.125 in |
Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 204 °C | 379 - 399 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Medium Heat Resistance | |
| Medium Impact Resistance | ||
| Forms | Powder | |
| Generic Material | PVC Alloy | |
| Generic Name | Polyvinyl Chloride Alloy (PVC Alloy) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 11445 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Building Materials | |
| Siding Substrate |
Users viewing this material also viewed the following:
- Polimeri Europa Greenflex® ML 21 Ethylene Vinyl Acetate Copolymer - Injection Molding
- PolyMirae Moplen HP420J BDDP Film Grade Polypropylene
- DuPont Fusabond® MN493D Ethylene Octene Copolymer (discontinued **)
- Polykemi AB POLYfill PPC 12000 Polypropylene Copolymer
- Quadrant EPP Semitron® ESd 225 POM-C, static dissipative, extruded (ISO Data)
- Inno-Comp INNOPOL® CS 3-9230 KAR BU UV-Stabilized, 26% Mineral-Filled Compound Blend Of Polypropylene Homopolymer And Block-Copolymer
- SK Chemicals SKYPEL G182D General Grade
- Fainplast Compounds GS 65 Flexible PVC, Injection Molding for Footwear
- 3M 32662 Black Heavy Duty Performance Coating - Part B
- Asahi Kasei Xyron® X0715 Modified Polyphenylene Ether
Copyright © lookpolymers.com All Rights Reserved