PolyOne Geon™ 81510 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ 81510 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D792 |
| Spiral Flow | 94.0 cm | 37.0 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 86 | 86 | ASTM D2240 |
| Tensile Strength, Yield | 75.8 MPa | 11000 psi | Type I, 51 mm/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 51 mm/min; ASTM D638 |
| Tensile Modulus | 5.52 GPa | 801 ksi | Type I, 51 mm/min; ASTM D638 |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 5.17 GPa | 750 ksi | ASTM D790 |
| Poissons Ratio | 0.42 | 0.42 | ASTM E132 |
| Shear Modulus | 1.94 GPa | 281 ksi | Calculated |
| Izod Impact, Notched | 0.530 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.993 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Izod Impact, Unnotched | 2.10 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
3.93 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 31.0 µm/m-°C | 17.2 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.1 °C @Thickness 6.35 mm |
169 °F @Thickness 0.250 in |
Annealed; ASTM D648 |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746 |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746 |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
ALL; UL 94 |
| 5VA @Thickness 1.50 mm |
5VA @Thickness 0.0591 in |
ALL; UL 94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 199 - 210 °C | 390 - 410 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | NSF 61 | |
| Features | General Purpose | |
| High Flow | ||
| Filler / Reinforcement | Glass Fiber Reinforcement, 10% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Fluid Handling | |
| General Purpose |
Users viewing this material also viewed the following:
- Plaskolite Optix® CP - 71 General Purpose Acrylic Resin
- PEAK Werkstoff DISPAL S270 Aluminum Alloy, AlSi25Fe4Ni3CuMgMnCrTi, Condition T6
- SolVin 372NA Polyvinyl Chloride Low Viscosity Paste
- Saint-Gobain Chemlam® Silver 12 Wear Resistant Industrial Laminate
- SABIC Innovative Plastics LNP THERMOCOMP RX96592 PA 66
- Eurotec® Tecodur® PB70 GB30 NL PBT, 30% glass bead reinforced, natural
- Asahi Kasei Thermofil P-20TC-1156 20% Talc Filled, Heat Stabilized
- Asahi Kasei Thermylene® P7-20FG-0876 Chemically Coupled Polypropylene Compound, 20% Glass Filled
- Solvay RHEOZAN SH Biopolymer
Copyright © lookpolymers.com All Rights Reserved