- PolyOne Edgetek® SY-03CF/000 Polystyrene - High Impact (HIPS), Carbon Fiber Reinforced (discontinued **)
PolyOne Edgetek® SY-03CF/000 Polystyrene - High Impact (HIPS), Carbon Fiber Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , Polystyrene (PS) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® SY-03CF/000 Polystyrene - High Impact (HIPS), Carbon Fiber Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedUL 94 HB (HEM TEST)PolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.046 g/cc | 1.046 g/cc | ASTM D792 |
| Water Absorption | 0.040 % | 0.040 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 30.99 MPa | 4495 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Modulus | 2.38 GPa | 345 ksi | ASTM D790 |
| Izod Impact, Notched | 0.731 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.37 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.4 µm/m-°C @Temperature 20.0 °C |
28.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | >= 0.144 W/m-K | >= 1.00 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.6 °C | 195 °F | Annealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 232 - 260 °C | 450 - 500 °F | Molding |
| Mold Temperature | 37.8 - 71.1 °C | 100 - 160 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Nye Lubricants 368AS (RL) Synthetic Oil
- Mallard Creek Polymers Rovene® 6118 Styrene-Acrylic Emulsion
- Materion BrushCAST® 275CT Fine Grain Casting Alloy (As Cast)
- Covestro Desmopan® KU 2-8671 Polyurethane
- EMS-Grivory Grivory® BG-30 S PA6-GF30
- DuPont Performance Polymers Crastin® LW9320 BK851 PBT+SAN (Unverified Data**)
- DuPont Teijin Films Melinex® 623 Polyester Film, 700 Gauge
- Eurostar Starpylen HU 30BF4 PP, 30% Bamboo Fiber Filled, Injection Molding
- 3M 201+ General Use Masking Tape
- 3M 93010LE High Strength Double Coated Tape with Adhesive 300LSE
Copyright © lookpolymers.com All Rights Reserved