PolyOne Edgetek® PC-30CF/000 BLACK Polycarbonate (PC)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Edgetek® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® PC-30CF/000 BLACK Polycarbonate (PC).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.030 cm/cm @Thickness 3.18 mm |
0.010 - 0.030 in/in @Thickness 0.125 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.0090 cm/cm @Thickness 3.18 mm |
0.0080 - 0.0090 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 172 MPa | 24900 psi | 5.1 mm/min; ASTM D638 |
| Elongation at Break | 1.0 - 2.0 % | 1.0 - 2.0 % | ASTM D638 |
| Tensile Modulus | 20.2 GPa | 2930 ksi | 5.1 mm/min; ASTM D638 |
| Flexural Strength | 255 MPa | 37000 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 17.0 GPa | 2470 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.750 J/cm | 1.41 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 136 °C | 277 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 - 10000 ohm-cm | 100 - 10000 ohm-cm | ASTM D257 |
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Amorphous | |
| Electrically Conductive | ||
| Good Dimensional Stability | ||
| High Stiffness | ||
| Filler / Reinforcement | Carbon Fiber Reinforcement, 30% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | PC | |
| Generic Name | Polycarbonate (PC) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Business Equipment | |
| Communication Applications | ||
| Electrical Housing | ||
| Electrical/Electronic Applications | ||
| Housings |
Users viewing this material also viewed the following:
- Northstar Polymers MPS-F04A Hand-Mixable Flexible Foam
- Lehmann & Voss LUVOCOM® 1-7985 Polyamide 66, with aramid reinforcement and PTFE, heat stabilized
- Lehmann & Voss LUVOCOM® 1/CF/15/HS Polyamide 66, with carbon fiber, heat stabilized
- Samyang Triloy® 210NH PC/ABS alloy, Flame Retardant
- TIMCAL TIMREX® PP 25 Natural Flake Graphite
- Chang Chun Plastic Longlite PM T308J General Purpose Phenolic Molding Compound
- Beijing Ranger Chem PBT 403 M-G20 Heat Resistant and Environmental Protection Flame Retarding FR PBT
- Bulk Molding Compounds BMC 610 - SP Mineral Filled, Glass Reinforced Polyester Compound, with UV Stabilizer
- Mateck Thallium Bromoiodide TIBr-TII (KRS-5)
Copyright © lookpolymers.com All Rights Reserved