PolyOne Edgetek® ES-40CF/000 Polyethersulfone - 40% Carbon Fiber Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® ES-40CF/000 Polyethersulfone - 40% Carbon Fiber Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Water Absorption | 0.30 % @Thickness 3.17 mm |
0.30 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 221 MPa | 32000 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
| Elongation at Break | 2.0 - 3.0 % | 2.0 - 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 22.1 GPa | 3200 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 296 MPa | 43000 psi | ASTM D790 |
| Flexural Modulus | 22.1 GPa | 3200 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
2.00 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 420 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 371 - 399 °C | 700 - 750 °F | Molding |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable W1213 Polyvinyl Chloride, Flexible (PVC, Flexible)
- MV Labs PR300 Pr2(CO3)3·8H2O Praseodymium carbonate hydrate
- Omni Plastics OmniLon™ 6 PA6 GR33 NA Glass Reinforced Nylon
- Inno-Comp INNOPOL® CS 1-4140 BAP 40% Talc-Filled Polypropylene Homopolymer
- SABIC Innovative Plastics LNP THERMOCOMP DX06412H PC
- Plenco 1581 Polyester, Pellet, Injection Molded
- DSM Akulon® K222-KGV5
- DSM Arnite® AV2 370 XL-T PET-GF35
- BASF Ultramid® 8232G HS FR 25% Glass Fiber Fire Retardant PA6 (Dry)
- Chevron Phillips 6109L LLDPE Blown Film Resin, Butene Copolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved