- PolyOne Edgetek® CY-10GF/000 UV FR V0 NATURAL PC/ABS Blend, Glass Filled (discontinued **)
PolyOne Edgetek® CY-10GF/000 UV FR V0 NATURAL PC/ABS Blend, Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® CY-10GF/000 UV FR V0 NATURAL PC/ABS Blend, Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedNon-HalogenatedFlame RetardantUL 94 V0PolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 74.60 MPa | 10820 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 5.5 % | 5.5 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 4.238 GPa | 614.7 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 118.67 MPa | 17212 psi | ASTM D790 |
| Flexural Modulus | 3.86 GPa | 560 ksi | ASTM D790 |
| Izod Impact, Notched | 0.520 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.974 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | Annealed, 0.125 in bars; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | All Colors; 0.063 in. |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 232 - 260 °C | 450 - 500 °F | Molding |
| Mold Temperature | 82.2 - 93.3 °C | 180 - 200 °F | |
| Drying Temperature | 93.3 °C | 200 °F | |
| Dry Time | 4 hour | 4 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- PolyOne Versaflex™ OM 6275-1 Thermoplastic Elastomer (TPE)
- Pyrotek TS-103 Thermoset Electrical Insulation Product (Nema Grade: G-3)
- Permabond HL126 Anaerobic Threadlocker
- Victrex® PEEK -HT™ G22 PolyEtherKetone, Unreinforced
- Lehmann & Voss LUVOCOM® 1-7817 Polyamide 66, with carbon fiber, lubricant modified, heat stabilized
- LATI Latistat 52/7-02 MI/30 PP Homopolymer, 30% Mica Filled
- Teknor Apex APEX® 3201-80 Polyvinyl Chloride, Flexible
- Alcoa Excalibar® 6013-T8 Aluminum, 3.8-8.2 cm diameter
- Chang Chun Plastic PBT4130 Fire Retardant & 30% Glass Fiber Enforced Grade PBT
- Teknor Apex Monprene® MP 1579 Thermoplastic Elastomer
Copyright © lookpolymers.com All Rights Reserved