Polimeri Europa Riblene® FF 34 Low Density Polyethylene - Blown Film Extrusion

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer	Polimeri Europa (Former EniChem)
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polimeri Europa Riblene® FF 34 Low Density Polyethylene - Blown Film Extrusion.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Riblene FF 34 is a high molecular weight low density polyethylene (LDPE), with added slip and antiblocking agents, suitable for blown film extrusion. Riblene FF 34 is characterized by a good melt strength leading to a good bubble stability during extrusion.Films manufactured with Riblene FF 34 are easily heat shrinkable and characterized by good mechanical properties.Main Applications: Riblene FF 34 is recommended for the production of general packaging film, shoppers, lamination film and blend.Information provided by Polimeri Europa.

Physical Properties	Metric	English	Comments
Specific Gravity	0.924 g/cc	0.924 g/cc	ISO 1183
Thickness	30.0 - 150 microns	1.18 - 5.91 mil	Recommended
Melt Flow	0.75 g/10 min @Load 2.16 kg, Temperature 190 °C	0.75 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	10.0 MPa	1450 psi	ISO 527-3
Film Tensile Strength at Yield, TD	11.0 MPa	1600 psi	ISO 527-3
Film Elongation at Break, MD	400 %	400 %	ISO 527-3
Film Elongation at Break, TD	600 %	600 %	ISO 527-3
Coefficient of Friction, Dynamic	0.15	0.15	ISO 8295
Elmendorf Tear Strength, MD	4.5855 g/micron	116.47 g/mil	ISO 6383-2
Elmendorf Tear Strength, TD	6.114 g/micron	155.3 g/mil	ISO 6383-2
Dart Drop Test	180 g	0.397 lb	F50; ISO 7765-1
Film Tensile Strength at Break, MD	22.0 MPa	3190 psi	ISO 527-3
Film Tensile Strength at Break, TD	19.0 MPa	2760 psi	ISO 527-3
1% Secant Modulus, MD	180 MPa	26100 psi	ISO 527-3
1% Secant Modulus, TD	190 MPa	27600 psi	ISO 527-3

Thermal Properties	Metric	English	Comments
Melting Point	114 °C	237 °F	Internal method
Vicat Softening Point	95.0 °C @Load 1.00 kg	203 °F @Load 2.20 lb	ISO 306/A
Brittleness Temperature	<= -75.0 °C	<= -103 °F	ASTM D746

Optical Properties	Metric	English	Comments
Haze	9.0 %	9.0 %	ISO 14782
Gloss	60 %	60 %	45°; ASTM D2457