Polimeri Europa EDISTIR N1841 Polystyrene (discontinued **)
| Category | Polymer , Thermoplastic , Polystyrene (PS) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polimeri Europa EDISTIR N1841 Polystyrene
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Symbol according to ISO 1043-1: PS Designation: Thermoplastic ISO 1622-PS,M,085-12 General purpose polystyrene combining easy flow and medium heat. This grade exhibits excellent processability in injection molding and should be used for complex and thin-wall parts and for fast-cycle moldings. Applications: Typical uses are beverage cups, point of sales, containers for foods and cosmetics, toys, housewares, medical articles (Petri dishes).Unfilled. Suitable for Injection Molding. Supplied as pellets. Contains release agent.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Melt Flow | 10 g/10 min @Load 5.00 kg, Temperature 200 °C |
10 g/10 min @Load 11.0 lb, Temperature 392 °F |
cm³/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 39.0 MPa | 5660 psi | 5 mm/min |
| Elongation at Break | 1.8 % | 1.8 % | 5 mm/min |
| Tensile Modulus | 3.25 GPa | 471 ksi | 1 mm/min |
| Charpy Impact Unnotched | 1.00 J/cm² | 4.76 ft-lb/in² | |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | |
| Vicat Softening Point | 86.0 °C | 187 °F | 50°C/hr; 50N |
| Glass Transition Temp, Tg | 90.0 °C | 194 °F | 10°C/min test |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 80 % | 80 % | Manufacturer specifies 'transparent' but doesn't quantify. |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
|
| Dielectric Strength | 70.0 kV/mm | 1780 kV/in | |
| Dissipation Factor | 0.00020 @Frequency 100 Hz |
0.00020 @Frequency 100 Hz |
|
| Comparative Tracking Index | 375 V | 375 V |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 8599 BLK
- Quadrant EPP Ketron® TX PEEK + solid lubricant, extruded (ISO Data)
- DuPont Performance Polymers Delrin® SC655 NC010 Acetal Homopolymer (Unverified Data**)
- Latrobe LSSâ„¢ 135M Nitriding Steel (ASTM A355 Class A)
- SABIC Innovative Plastics NORYL GTX GTX987 PPE+PA66 (Asia Pacific)
- Wall Colmonoy COLMONOY® 635 - Nickel-Chromium-Boron Matrix Alloy With Tungsten Carbide
- A. Schulman PP 1116-01 Polypropylene Molding Grade Copolymer Polypropylene
- Lubrizol Estane® 2102-90A Thermoplastic Polyurethane Elastomer
- ALIMEX ACP 6000 Aluminum Cast Plate
Copyright © lookpolymers.com All Rights Reserved