Polimeri Europa Clearflex® H&T CLH 150 Linear Low Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Clearflex® H&T
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Clearflex® H&T CLH 150 Linear Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Clearflex H&T CLH 150 is a linear low density polyethylene resin, with antioxidants, suitable for cast film extrusion.Stretch films obtained from Clearflex H&T CLH 150 show good optical properties, high puncture and dart resistance together with optimum performances in automatic wrapping machines (pre-stretch).Main Applications: Clearflex H&T CLH 150 is recommended to produce medium/high pre-stretch film. Moreover, the combination of high mechanical properties and low gel content, together with a low cling effect, makes Clearflex H&T CLH 150, even pure, the right choice in coextruded structures to produce high performance thin stretch film.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.919 g/cc
0.919 g/cc
ISO 1183
Thickness 8.00 - 50.0 microns
0.315 - 1.97 mil
Recommended
Melt Flow 2.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.0 MPa
1450 psi
ISO 527-3
Film Tensile Strength at Yield, TD 10.0 MPa
1450 psi
ISO 527-3
Film Elongation at Break, MD 400 %
400 %
ISO 527-3
Film Elongation at Break, TD 600 %
600 %
ISO 527-3
Coefficient of Friction, Dynamic >= 0.50
>= 0.50
ISO 8295
Elmendorf Tear Strength, MD 10.19 g/micron
258.8 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 15.285 g/micron
388.24 g/mil
ISO 6383-2
Dart Drop Test 180 g
0.397 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 30.0 MPa
4350 psi
ISO 527-3
Film Tensile Strength at Break, TD 25.0 MPa
3630 psi
ISO 527-3
1% Secant Modulus, MD 130 MPa
18900 psi
ISO 527-3
1% Secant Modulus, TD 140 MPa
20300 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 120 °C
248 °F
Internal method
Vicat Softening Point 95.0 °C

@Load 1.00 kg
203 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -70.0 °C
<= -94.0 °F
ASTM D746
Optical Properties Metric English Comments
Haze 1.0 %
1.0 %
ISO 14782
Gloss 91 %
91 %
45°; ASTM D2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified