Plenco 7591 Phenolic, Pellet, Transfer Molded
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Mineral/Flock Filled |
| Manufacturer | Plenco (Plastics Engineering Company) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plenco 7591 Phenolic, Pellet, Transfer Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PLENCO 07591 is a mineral and flock cotton filled novolac phenolic molding compound. UL recognized under component file E40654.Information supplied by Plenco.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.610 g/cc | 0.0220 lb/in³ | ASTM D1895 |
| Density | 1.46 g/cc | 0.0527 lb/in³ | ASTM D792 |
| Water Absorption | 0.18 % | 0.18 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0057 cm/cm | 0.0057 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell E | 77 | 77 | ASTM D785 |
| Tensile Strength, Ultimate | 37.0 MPa | 5370 psi | ASTM D638 |
| Elongation at Break | 0.53 % | 0.53 % | ASTM D638 |
| Tensile Modulus | 8.40 GPa | 1220 ksi | ASTM D638 |
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D790 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ASTM D790 |
| Compressive Strength | 175 MPa | 25400 psi | ASTM D695 |
| Izod Impact, Notched | 0.310 J/cm | 0.581 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.310 J/cm² | 1.48 ft-lb/in² | ASTM D256 |
| Impact | 150 | 150 | J/m Drop Ball Impact; PLENCO |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 190 °C | 374 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 178 °C | 352 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 4.30 mm |
V-0 @Thickness 0.169 in |
|
| Oxygen Index | 33 % | 33 % | ASTM D2863 |
| Shrinkage | 0.29 % | 0.29 % | 72 hr, 120ºC; ASTM D1299 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.60e+10 ohm-cm | 3.60e+10 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.9 | 5.9 | ASTM D150 |
| Dielectric Strength | 6.30 kV/mm | 160 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.071 | 0.071 | ASTM D150 |
| Arc Resistance | 179 sec | 179 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
Users viewing this material also viewed the following:
- NOVA Chemicals Novapol® PP-0118-F LLDPE Extrusion Resin
- Loxim 100 00V0 Polycarbonate, Flame Retardant
- Haynes 230® alloy, 40% cold reduction, 1066°C anneal for 5 minutes
- LATI Latamid 6 H2 G/65 PA 6, 65% Glass Fiber Reinforced, Heat Stabilized
- Silberline Extra Sparkle Silvex® 400-10-C
- Borealis Xmod™ GD301FE Polypropylene, Glass Fiber Reinforced
- Tra-Con Tra-Bond 2110 High Impact Epoxy Staking Compound
- Loctite® PRISM® 4210 Instant Adhesive
- Ashley Polymers Ashlene® 1621 Polycarbonate
- Alliance Polymers Viprene™ G40D-22U-BLK Thermoplastic Vulcanizate Elastomer
Copyright © lookpolymers.com All Rights Reserved