Plenco 302 Black Impact Grade Woodflour/Flock Filled Phenolic Molding Compound  (discontinued **)

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Impact Grade, Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plenco 302 Black Impact Grade Woodflour/Flock Filled Phenolic Molding Compound  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plaslok 302 is a two-stage, woodflour and flock-filled phenolic molding compound. It has low specific gravity, broad molding latitude and an excellent balance of electrical and physical properties. Its high impact strength makes it particularly well suited for thin wall parts, or where mechanical stress is experienced during assembly.Data provided by Plaslok Corporation.Plaslok Corporation was purchased by Plastics Engineering Company in March 2000. The Plaslok name is no longer used on any products.
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
ASTM D792
Apparent Bulk Density 0.500 g/cc
0.0181 lb/in³
ASTM D1895
Water Absorption 0.80 %
0.80 %
ASTM D570
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
Compression; ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 41.0 MPa
5950 psi
ASTM D638
Flexural Yield Strength 76.0 MPa
11000 psi
ASTM D790
Flexural Modulus 6.90 GPa
1000 ksi
ASTM D790
Compressive Yield Strength 207 MPa
30000 psi
ASTM D695
Izod Impact, Notched 0.270 J/cm
0.506 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 166 °C
331 °F
ASTM D648
UL RTI, Electrical 150 °C

@Thickness 1.57 mm
302 °F

@Thickness 0.0618 in
UL RTI, Mechanical with Impact 150 °C

@Thickness 1.57 mm
302 °F

@Thickness 0.0618 in
UL RTI, Mechanical without Impact 150 °C

@Thickness 1.57 mm
302 °F

@Thickness 0.0618 in
Flammability, UL94 V-2

@Thickness 3.18 mm
V-2

@Thickness 0.125 in
V-2

@Thickness 3.18 mm
V-2

@Thickness 0.125 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
ASTM D257
Dielectric Constant 4.2

@Frequency 1e+6 Hz
4.2

@Frequency 1e+6 Hz
ASTM D150
6.8

@Frequency 60 Hz
6.8

@Frequency 60 Hz
ASTM D150
Dielectric Strength 12.2 kV/mm
310 kV/in
ASTM D149
Dissipation Factor 0.050

@Frequency 1e+6 Hz
0.050

@Frequency 1e+6 Hz
ASTM D150
0.20

@Frequency 60 Hz
0.20

@Frequency 60 Hz
ASTM D150
Comparative Tracking Index 138 V
138 V
UL 746