Plaskolite Optix® CP - 1000 I High Impact Grade Acrylic Resin
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Impact Modified, Molded , Acrylic, Optical Grade, Molded |
| Manufacturer | Plaskolite |
| Trade Name | Optix® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plaskolite Optix® CP - 1000 I High Impact Grade Acrylic Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
OPTIX® impact-modified grades offer 7 to 10 times the impact resistance of general purpose polymers while maintaining optical clarity.Information provided by Plaskolite, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D-792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D-955 |
| Melt Flow | 2.8 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.8 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 42.1 MPa | 6100 psi | ASTM D-638 |
| Elongation at Break | 37 % | 37 % | ASTM D-638 |
| Modulus of Elasticity | 2.03 GPa | 295 ksi | ASTM D-638 |
| Flexural Strength | 61.4 MPa | 8900 psi | ASTM D-790 |
| Izod Impact, Notched | 0.587 J/cm @Thickness 6.35 mm |
1.10 ft-lb/in @Thickness 0.250 in |
ASTM D-256 |
| Gardner Impact | 5.54 J @Thickness 3.17 mm |
4.08 ft-lb @Thickness 0.125 in |
Falling Weight; ASTM D-3029 GB |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 120 µm/m-°C | 66.7 µin/in-°F | ASTM D-696 |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | UL-746 ABC |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.8 °C | 172 °F | ASTM D-648 |
| Vicat Softening Point | 108 °C | 227 °F | ASTM D-1525 |
| Flammability, UL94 | HB | HB |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 1.8 % | <= 1.8 % | ASTM D-1003 |
| Transmission, Visible | 90.8 % | 90.8 % | ASTM D-1003 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| 3-Year Weathering | Listed | SAE J 576 (AMECA) |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 8502 P BLK , 37.5% Filler Content
- Omni Plastics OmniTuff™ HPP GRMF30 Homopolymer Polypropylene Glass/Mineral Filled
- SABIC Innovative Plastics Cycoloy® C7240P PC+ABS (Asia Pacific)
- Indium Corp. 1075-EX 30 VOC-Free Wave Solder Flux
- A. Schulman PP 1259 Polypropylene Medium Impact Polypropylene
- Washington Penn Medium Impact Copolymer 40% Calcium Carbonate Filled
- A. Schulman POLYBATCH™ Silver 7002/5 Concentrate Based In LDPE
- Aclo Accutech Polypropylene Copolymer CP0437C40L1 Calcium Reinforced
- PolyOne Synprene® IT38-034 Thermoplastic Elastomer - SBC (discontinued **)
- SABIC Innovative Plastics NORYL CN5260 PPE+PS (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved