Phillips 66 COPYLENE® CH200LN-02 Polypropylene, Homopolymer, Rx grade, Nucleated, Lube, Injection Molding

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Phillips 66
Trade Name	COPYLENE®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Phillips 66 COPYLENE® CH200LN-02 Polypropylene, Homopolymer, Rx grade, Nucleated, Lube, Injection Molding.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

COPYLENE™ CH200LN-02 is a polypropylene homopolymer resin nucleated for faster crystallization with antistatic properties and designed for injection molding applications. Applications: Caps & Closures, Sports, Leisure and Toys, Housewares, Opaque Containers. Equivalent to Pro-fax® HL232RInformation provided by Phillips 66.

Physical Properties	Metric	English	Comments
Density	0.902 g/cc	0.0326 lb/in³	ASTM D792
Melt Flow	20 g/10 min @Load 2.16 kg, Temperature 230 °C	20 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	90	90	ASTM D785
Tensile Strength, Yield	37.9 MPa	5500 psi	2 in/min; ASTM D638
Elongation at Yield	7.5 %	7.5 %	ASTM D638
Flexural Modulus	1.72 GPa	250 ksi	0.05 in/min; 1% secant; Procedure A; ASTM D790
Izod Impact, Notched	0.320 J/cm @Temperature 23.0 °C	0.600 ft-lb/in @Temperature 73.4 °F	Method A; ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	124 °C	255 °F	unannealed; ASTM D648

Descriptive Properties	Value	Comments
Process	Injection Molding
Region	Mexico	Bamberger Polymers Distribution
	US & Canada	Bamberger Polymers Distribution