Petroquimica Triunfo Trithene® TS 3003 LDPE - Film Grade

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Petroquimica Triunfo
Trade Name Trithene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Petroquimica Triunfo Trithene® TS 3003 LDPE - Film Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Trithene® TS 3003 resin is a low-density, high molecular weight polyethylene that offers high mechanical strength and excellent optical properties. The product shows high modulus of elasticity, that it offers the property of recovering the original shape when finished the deformation strength. Additionally, because of its molecular structure, Trithene® TS 3003 resin shows excellent performance in conventional extruders and low energy consumption during processing, allowing the production of films with high thickness uniformity and good appearance. The additive package warrants thermal stability, low blocking, and adequate coefficient of friction - COF, which are required to allow high productivity on the extrusion, printing and finishing lines. This product complies with ASTM standard D1248-IIA5 and the requirements of Brazilian and corresponding legislation of Mercosul and it is in conformity with FDA Regulations 21 CFR 177.1520 (c) 2.1, to contact with foodstuff. Applications: Film for sleeve label to different kinds of bottles (soft drink, milk, mineral water, eatable oil, lubricants and hygiene products and cleanness). Shrink film with high gloss and mechanical strength. Grade for very stiff and transparent film.Resin Properties: Compressed molded plate. Method ASTM D-1928, procedure C. Film obtained on a 50mm blow film line with barrier screw, 25:1 L/D, 1.0mm die gap, 50µm gauge, 2.3:1 BUR.Information provided by Dax Resinas
Physical Properties Metric English Comments
Density 0.925 - 0.927 g/cc
0.0334 - 0.0335 lb/in³
ASTM D1505
Thickness 50.0 microns
1.97 mil
Melt Index of Compound 0.23 - 0.30 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.23 - 0.30 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 16.0 MPa
2320 psi
ASTM D638
Tensile Strength, Yield 12.0 MPa
1740 psi
ASTM D638
Film Elongation at Break, MD 325 %
325 %
ASTM D882
Film Elongation at Break, TD 675 %
675 %
ASTM D882
Elongation at Break 620 %
620 %
ASTM D638
Secant Modulus, MD 0.125 GPa
18.1 ksi
5%; ASTM D882
Secant Modulus, TD 0.130 GPa
18.9 ksi
5%; ASTM D882
Coefficient of Friction, Dynamic 0.090
0.090
ASTM D1894
Elmendorf Tear Strength, MD 6.80 g/micron
173 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 5.60 g/micron
142 g/mil
ASTM D1922
Dart Drop Test 200 g
0.441 lb
(method A); ASTM D1709
Film Tensile Strength at Break, MD 27.0 MPa
3920 psi
ASTM D882
Film Tensile Strength at Break, TD 24.0 MPa
3480 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 114 °C
237 °F
ASTM D3418
Optical Properties Metric English Comments
Gloss 96 %
96 %
@ 60° Gardner; ASTM D2457
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Processing Properties Metric English Comments
Processing Temperature 160 - 175 °C
320 - 347 °F
Plasticizing Zone
170 - 185 °C
338 - 365 °F
Mixture Zone
Feed Temperature 150 - 175 °C
302 - 347 °F
Adapter Temperature 180 - 195 °C
356 - 383 °F
Die Opening 0.0800 - 0.100 cm
0.0315 - 0.0394 in
Blow-up Ratio (BUR) 3.0
3.0
Recommended