Permabond TA4310 Toughened Acrylic Adhesive

Category	Polymer , Adhesive , Thermoset , Acrylic/Cyanoacrylate Adhesive
Manufacturer	Permabond
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Permabond TA4310 Toughened Acrylic Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

PERMABOND® TA4310 is a 2-part, 1:1 toughened acrylic adhesive. Its toughening makes it ideal for bonding dissimilar materials where differential thermal expansion and contraction could be an issue. It is easy to use with a delayed initiation, allowing accurate alignment of components. The strength develops quickly allowing clamps to be removed and a quick turnaround time when used in a production situation. Features & Benefits: Adhesion to a wide variety of substrates Fast cure at room temperature Easy to apply through static mixer nozzle High shear and peel strength Good impact strength Good chemical resistance Information provided by Permabond.

Physical Properties	Metric	English	Comments
Density	1.01 g/cc	0.0365 lb/in³	TA4310B
	1.05 g/cc	0.0379 lb/in³	TA4310A
Storage Temperature	2.00 - 7.00 °C	35.6 - 44.6 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength	28.0 MPa	4060 psi	DIN 53288
Adhesive Bond Strength	24.0 - 26.0 MPa	3480 - 3770 psi	Mild steel, Shear
Peel Strength	1.80 - 3.60 kN/m	10.3 - 20.5 pli	ISO 4578

Thermal Properties	Metric	English	Comments
CTE, linear	80.0 µm/m-°C	44.4 µin/in-°F	ASTM D696
Thermal Conductivity	0.100 W/m-K	0.694 BTU-in/hr-ft²-°F	ASTM C177

Electrical Properties	Metric	English	Comments
Volume Resistivity	2.00e+13 ohm-cm	2.00e+13 ohm-cm	ASTM D257
Dielectric Constant	4.6 @Frequency 1.00e+7 Hz	4.6 @Frequency 1.00e+7 Hz	ASTM D150
Dielectric Strength	30.0 - 50.0 kV/mm	762 - 1270 kV/in	ASTM D149

Processing Properties	Metric	English	Comments
Cure Time	10.0 - 15.0 min	0.167 - 0.250 hour	handling time
	25.0 - 30.0 min	0.417 - 0.500 hour	working strength
	1440 min	24.0 hour	full cure
Shelf Life	12.0 Month	12.0 Month

Descriptive Properties	Value	Comments
Appearance	Brown TA4310B, Thixotropic paste	Uncured
	Off-white TA4310A, Thixotropic paste	Uncured
Maximum Gap Fill (mm)	2
Strength Retention	100% at 0°C	Relative to 0°C
	15% at 175°C	Relative to 0°C
	22% at 150°C	Relative to 0°C
	80% at 100°C	Relative to 0°C
	96% at 50°C	Relative to 0°C