Park Electrochemical Nelcote® F-529 Phenolic Prepreg, 3K PW Reinforced

Category	Polymer , Thermoset , Phenolic
Manufacturer	Park Electrochemical Corp.
Trade Name	Nelcote®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Park Electrochemical Nelcote® F-529 Phenolic Prepreg, 3K PW Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Nelcote® F-529 is a non-halogenated phenolic resin designed specifically for use in aircraft and mass-transit interior laminate and sandwich panels. F-529 was formulated for applications requiring non-halogenated FST (flame, smoke, toxicity) performance.Key Features and Benefits:Self-Adhesive resin system for sandwich panel applicationsNon-Halogenated and antimony-free resin formulationExcellent FST performanceLow OSU heat-release (< 20/20)Good Tack and Drape propertiesWhite color after cure for superior cosmeticsApplications/Qualifications:Aircraft InteriorsMass-Transit InteriorsMeets all requirements of:FAR 25.853FAR 25.856ATS 1000.001OSU 1990Information provided by Park Electrochemical Corp.

Physical Properties	Metric	English	Comments
Volatiles	<= 3.5 % @Temperature 135 °C	<= 3.5 % @Temperature 275 °F	8 min

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	531 MPa @Temperature 23.9 °C	77000 psi @Temperature 75.0 °F	0° Direction, Dry; Press Cure, 16min, 300°F; ASTM D638
Tensile Modulus	57.2 GPa @Temperature 23.9 °C	8300 ksi @Temperature 75.0 °F	0° Direction, Dry; Press Cure, 16min, 300°F; ASTM D638
Compressive Strength	696 MPa @Temperature 23.9 °C	101000 psi @Temperature 75.0 °F	Dry; Press Cure, 16min, 300°F; ASTM D695
Compressive Modulus	54.5 GPa @Temperature 23.9 °C	7900 ksi @Temperature 75.0 °F	Dry; Press Cure, 16min, 300°F; ASTM D695

Optical Properties	Metric	English	Comments
Optical Density	1.0	1.0	Dm, Flaming Mode; FAR 25.853, Part 25 Appendix F, Part V

Processing Properties	Metric	English	Comments
Gel Time	7.00 min	7.00 min
Shelf Life	6.00 Month @Temperature 4.44 °C	6.00 Month @Temperature 40.0 °F

Descriptive Properties	Value	Comments
Burn Length (in)	1.8	Vertical Burn, 60 sec; FAR 25.853, Part 25 Appendix F, Part I (b) (4)
Climbing Drum Peel (in-lb/3in)	8	ASTM D1781; Dry, 75°F; Press Cure, 16min, 300°F
Drip	None	Vertical Burn, 60 sec; FAR 25.853, Part 25 Appendix F, Part I (b) (4)
Fabric Area Weight (g/m²)	193
Heat Release, Peak (KW/m²)	32	FAR 25.853 Part 25 Appendix F, Part IV
Heat Release, Total (KW-min/m²)	19	FAR 25.853 Part 25 Appendix F, Part IV
Prepreg Resin Content (%)	38-44
Resin Flow (%)	10-30	260°F, 150psi
Self Extinguish Time (sec)	0	Vertical Burn, 60 sec; FAR 25.853, Part 25 Appendix F, Part I (b) (4)

Users viewing this material also viewed the following: